- Polymer Property : CTE, linear = 15.4 µm/m-°C
Polymer Property : CTE, linear = 15.4 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.4 µm/m-°C @Temperature 20.0 - 800 °C |
8.56 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes Waspaloy™ alloy, sheet Age-hardenable superalloy with very good strength at temperatures up 980°C (1800°F), can be cold-formed in the annealed condition, may also be hot formed at 1040°C (1900°F) and above, go.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 30% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 50% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 15.4 µm/m-°C @Temperature 25.0 - 700 °C |
8.56 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||