Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 9.00 µm/m-°C @Temperature 25.0 °C |
5.00 µin/in-°F @Temperature 77.0 °F |
|
Mykroy/Mycalex MM 800 Machining Grade Glass-bonded Mica Composite MM 800 (formerly MM 1600) is a compression molded glass mica composite that is the perfect alternative to high performance plastics where high temperature, good dielectric strength and good arc resi.. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature -55.0 - 288 °C |
5.00 µin/in-°F @Temperature -67.0 - 550 °F |
Y-Direction; ASTM D3386-94 |
Rogers Corporation RO4835 Hydrocarbon Ceramic Laminate, Improved Oxidation Resistance Features and Benefits:Significantly improved oxidation resistance compared to typical thermoset microwave materialsDesigned for performance sensitive, high volume applicationsLow loss - Excellent el.. |
|||
CTE, linear | 9.00 - 13.0 µm/m-°C @Temperature -40.0 - 125 °C |
5.00 - 7.23 µin/in-°F @Temperature -40.0 - 257 °F |
X/Y; IPC-TM-650.2.4.41 |
Park Electrochemical Nelco® N4000-13 SI® High-Speed Multifunctional Epoxy Laminate and Prepreg The Nelco® N4000-13 series is an enhanced epoxy resin system engineered to provide both outstanding thermal and high signal speed / low signal loss properties. N4000-13 SI® is excellent for applic.. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 100 - 200 °C |
5.00 µin/in-°F @Temperature 212 - 392 °F |
Axial; ASTM E831 |
Solvay Specialty Polymers Ryton® R-4-230NA Polyphenylene Sulfide Compound
(Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® R-4-230NA is an advanced 40% fiberglass reinforced polyphenylene sulfide compound which provides reduced flash and improved processability compare.. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 20.0 - 300 °C |
5.00 µin/in-°F @Temperature 68.0 - 572 °F |
|
H.C. Starck WCu 75/25 Tungsten-Copper Composite Material Description of Product: Tungsten-copper composite materials are produced by copper infiltration of porous sintered tungsten. They are available with different copper contents (10 - 30 %). A therm.. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 20.0 - 300 °C |
5.00 µin/in-°F @Temperature 68.0 - 572 °F |
|
Schott BG4 Band Pass Filter Ionically colored glass. Data provided by the manufacturer, Schott Glas Mainz. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 20.0 - 300 °C |
5.00 µin/in-°F @Temperature 68.0 - 572 °F |
|
Schott N-BAK2 Glass Information Provided by SCHOTT North America, Inc. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature -30.0 - 70.0 °C |
5.00 µin/in-°F @Temperature -22.0 - 158 °F |
|
Schott N-SF6 Glass Information Provided by SCHOTT North America, Inc. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 20.0 - 300 °C |
5.00 µin/in-°F @Temperature 68.0 - 572 °F |
|
Schott SF5 Glass Information Provided by SCHOTT North America, Inc. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 20.0 - 300 °C |
5.00 µin/in-°F @Temperature 68.0 - 572 °F |
|
Schott SF6 Glass Information Provided by SCHOTT North America, Inc. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 20.0 - 300 °C |
5.00 µin/in-°F @Temperature 68.0 - 572 °F |
|
Schott SF6HT Glass Information Provided by SCHOTT North America, Inc. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 20.0 - 1000 °C |
5.00 µin/in-°F @Temperature 68.0 - 1830 °F |
DIN EN 821-1 |
CeramTec DN 70 Dispersion Ceramic, Al2O3-ZrO2 DN 70 is a ZTA Alumina Toughened Zirconia. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Rod Medium To High Strength General-Purpose Alloy. Tensile property data below is typical of rod; more specific form/thickness entries are also available in MatWeb.Industry Specifications: USA Aeros.. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Rod or Thickness, Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to Rod or Thickness, |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Rod or Thickness, Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to Rod or Thickness, |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Rod or Thickness, 4.00-6.00 in, Annealed, Per Mil-T-9047G Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to Rod or Thickness, 4.00-6.00 in, Annealed, Per Mil-T-9047G; other specific form/thickness entries .. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Sheet and Plate, 0.025-1.000 in, Annealed, Per ASTM B265 Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to Sheet and Plate, 0.025-1.000 in, Annealed, Per ASTM B265; other specific form/thickness entries a.. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5), Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5), >0.500-1.000 in, STD, Per Mil-T-9047G Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to >0.500-1.000 in, STD, Per Mil-T-9047G; other specific form/thickness entries are also available i.. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5), >1.000-1.500 in, STD, Per Mil-T-9047G Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to >1.000-1.500 in, STD, Per Mil-T-9047G; other specific form/thickness entries are also available i.. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
TIMET 6-4 Titanium Alloy (Ti-6Al-4V-0.1Ru; ASTM Grade 29) Medium To High Strength General-Purpose Alloy. Property data below are typical of Timet® 6-4 ELI (without Ru). The 0.1 Ru ELI variant is used for enhanced corrosion resistance.Data provided by TI.. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
TIMET TIMETAL® 6-4 ELI Titanium Alloy (Ti-6Al-4V ELI; ASTM Grade 23) (Annealed; Medium To High Strength General-Purpose Alloy Minimum tensile property data below are specific to this MatWeb entry; other specific form/thickness entries are also available in MatWeb.Features: A .. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
TIMET TIMETAL® 6-4 ELI Titanium Alloy (Ti-6Al-4V ELI; ASTM Grade 23) (Annealed; 2.50 - 4.00 in Rod or Thickness; Per ASTM F136) Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to this MatWeb entry; other specific form/thickness entries are also available in MatWeb.Features: A.. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5), Rod, Square, or Hex, >1.500-2.000 in, Per Mil-T-9047G Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to Rod, Square, or Hex, >1.500-2.000 in, Per Mil-T-9047G; other specific form/thickness entries are .. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 21.0 - 100 °C |
5.00 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
Dura-Bar G2 Continuously Cast Gray Iron Bar Stock ASTM A48 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as an alternative to gray i.. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 250 °C |
5.00 µin/in-°F @Temperature 482 °F |
|
Ceramic Process Systems AlSiC-8, 70 vol% SiC Aluminum alloy A356.2 used. Hermeticity < 1x109 atm-cc/s He.CPS fabricates AlSiC by preparing an SiC preform which is subsequently infiltrated by molten aluminum metal. After infiltration, compone.. |
|||
CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
y direction; IPC TM-650 2.4.24 |
Arlon AD350A PTFE/Woven Fiberglass/Ceramic Filled Composite Tighter Dielectric Tolerance Low Z-Axis Thermal ExpansionCeramic Filled PTFEHigh Thermal ConductivityLarge Panel SizeBenefits:Higher Consistency of PerformanceSuperior PTH AdhesionHeat Dissipation a.. |