- Polymer Property : CTE, linear = 6.78 µin/in-°F
Polymer Property : CTE, linear = 6.78 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged at 649°C (1200°F) for 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 500 °C |
6.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 242® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 500 °C |
6.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 242® alloy, after 4000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 500 °C |
6.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and 40% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 500 °C |
6.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 500 °C |
6.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed, 40% cold work, aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 700 °C |
6.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes Hastelloy® B-3® alloy, 10% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 700 °C |
6.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes Hastelloy® B-3® alloy, 40% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 700 °C |
6.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes Hastelloy® B-3® alloy, 50% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 25.0 - 300 °C |
6.78 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Sheet, Cold Rolled and Solution Annealed HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 300 °C |
6.78 µin/in-°F @Temperature 68.0 - 572 °F |
|
| Schmolz + Bickenbach Thermodur® 2999 Hot Work Die Steel Description: Maximum high-temperature strength, good high-temperature wear resistance, excellent thermal shock resistance and thermal conductivity across the entire range of service temperatures App.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 21.0 - 300 °C |
6.78 µin/in-°F @Temperature 69.8 - 572 °F |
Mean |
| Dura-Bar 60-40-18 Continuously Cast Ductile Iron Bar Stock ASTM A536, 4018 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 300 °C |
6.78 µin/in-°F @Temperature 572 °F |
|
| Bohler-Uddeholm BÖHLER W303 ISODISC® Hot Work Tool Steel Description: Hot work tool steel featuring excellent hot tensile properties, high retention of hardness, good toughness and resistance to heat checking, admits water cooling. BOHLER W303 is also ava.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 300 °C |
6.78 µin/in-°F @Temperature 68.0 - 572 °F |
|
| Bohler-Uddeholm BÖHLER W403 VMR® Hot Work Tool Steel W403 VMR is a modified hot work alloy with an excellent combination of hot tensile properties and toughness. The balanced properties of this grade are not only due to chemistry modification, but to .. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature <=427 °C |
6.78 µin/in-°F @Temperature <=801 °F |
|
| AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition H 1075 AK Steel 15-5 PH® provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base metal and welds. Short-time, .. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature <=427 °C |
6.78 µin/in-°F @Temperature <=801 °F |
|
| AK Steel 17-4 PH® Precipitation Hardening Stainless Steel, Condition H 1075 AK Steel 17-4 PH® provides an outstanding combination of high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 21.0 - 649 °C |
6.78 µin/in-°F @Temperature 69.8 - 1200 °F |
|
| Carpenter Micro-Melt® 9 Hardened and Tempered Tool Steel Micro-Melt® 9 tool steel is a high vanadium tool steel produced using the Carpenter Micro-Melt powder process. This grade possesses wear resistance superior to most other tool steels along with goo.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 0.000 - 538 °C |
6.78 µin/in-°F @Temperature 32.0 - 1000 °F |
|
| ATI Allegheny Ludlum Stainless Steel AL 410S™ (UNS S41008) Allegheny Ludlum Al 410S™ stainless steel is a low-carbon modification of Type 410 stainless steel. Low carbon and optionally a small addition of titanium and /or columbium minimize austenite form.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 21.0 - 427 °C |
6.78 µin/in-°F @Temperature 69.8 - 801 °F |
|
| Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 1075 (Heated 579°C) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio.. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 204 °C |
6.78 µin/in-°F @Temperature 68.0 - 399 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||