Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 13.1 µm/m-°C @Temperature 30.0 - 300 °C |
7.30 µin/in-°F @Temperature 86.0 - 572 °F |
|
International Mold Steel PX5 Pre-Hardened Mold Steel (P20 Type) PX5 is a modified P20, high performance, high precision, mold steel. Unique Characteristics: Exceptionally clean steel with uniform microstructure – no pin holes, inclusions or hard spots. 30-3.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 21.1 - 649 °C |
7.30 µin/in-°F @Temperature 70.0 - 1200 °F |
|
Crucible Steel 161 Tool Steel, High Carbon H13 Crucible 161 is a high carbon modification of H13, intended for applications requiring higher hardness, compressive strength, wear resistance, or tempering resistance (hot hardness), at slightly low.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 21.1 - 649 °C |
7.30 µin/in-°F @Temperature 70.0 - 1200 °F |
|
Crucible Steel CPM® Nu-Die® EZ Tool Steel CRUCIBLE CPM Nu-Die EZ is a new, patented die and mold steel designed for service as die casting dies and plastic injection molds. It is supplied in the prehardened condition, and is easily machined.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 21.1 - 427 °C |
7.30 µin/in-°F @Temperature 70.0 - 800 °F |
|
Crucible Steel CSM® 21 17Cr-4Ni Precipitation Hardening Stainless Steel CSM 21 is a precipitation hardening stainless mold steel, providing outstanding corrosion resistance and toughness, good polishability, and moderate wear resistance, combined with simple heat treatm.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 21.1 - 649 °C |
7.30 µin/in-°F @Temperature 70.0 - 1200 °F |
|
Crucible Steel HALCOMB® 218 Tool Steel, AISI H11 Halcomb 218 is a general purpose hot work tool steel, combining good toughness with moderate high-temperature strength and heat check resistance. Because of its high toughness, it is particularly su.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 21.1 - 649 °C |
7.30 µin/in-°F @Temperature 70.0 - 1200 °F |
|
Crucible Steel PEERLESS A Tool Steel, AISI H21 Peerless A is designed for tools which will run hot, at operating temperatures between about 600F and 1100F. The tools should not be water cooled in service, due to a high risk of thermal shock. Pee.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 599 °C |
7.30 µin/in-°F @Temperature 1110 °F |
hardened to 45 HRC |
Bohler-Uddeholm ORVAR® 2M / AISI H13 Hot Work Tool Steel Orvar 2 Microdized is a chromium-molybdenum-vanadium alloyed steelORVAR® 2M / AISI H13 is a conventionally produced hot work tool steel with overall good ductility, toughness, wear resistance, hard.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 199 °C |
7.30 µin/in-°F @Temperature 68.0 - 390 °F |
hardness of 40 HRC |
Bohler-Uddeholm UDDEHOLM ALVAR 14 Hot Work Tool Steel Alvar 14 is a chromium-nickel-molybdenumvanadium alloyed steel ALVAR 14 is characterized by: Good toughnessGood resistance to high thermal stresses Good stability in hardeningGood through-hardening.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 599 °C |
7.30 µin/in-°F @Temperature 1110 °F |
hardened to 45 HRC |
Bohler-Uddeholm UDDEHOLM DIEVAR® Hot Work Tool Steel Description: Uddeholm Dievar is a high performance chromium-molybdenum-vanadium alloyed hot work tool steel which offers a very good resistance to heat checking, gross cracking, hot wear and plastic.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 599 °C |
7.30 µin/in-°F @Temperature 1110 °F |
hardened to 56 HRC |
Bohler-Uddeholm UDDEHOLM HOTVAR® Hot Work Tool Steel Molybdenum-vanadium alloyed steelHotvar® is a premium hot work steel developed by Uddeholm to provide very good performance in tooling up to 1200°F (650°C). The alloying elements in Hotvar® are .. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 599 °C |
7.30 µin/in-°F @Temperature 1110 °F |
hardened to 45 HRC |
Bohler-Uddeholm UDDEHOLM ORVAR® SUPERIOR (Premium AISI H13) Hot Work Tool Steel Chromium-molybdenum-vanadium alloyed steelA premium Cr-Mo-V-alloyed hot work die steel with good resistance to thermal fatigue. The steel is produced by a special melting and refining technique in o.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 599 °C |
7.30 µin/in-°F @Temperature 1110 °F |
hardened to 45 HRC |
Bohler-Uddeholm UDDEHOLM ORVAR® SUPREME (Premium AISI H13) Hot Work Tool Steel Chromium-molybdenum-vanadium alloyed steelA premium Cr-Mo-V-alloyed hot work die steel with good resistance to thermal fatigue. The steel is produced by a special melting and refining technique in o.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 599 °C |
7.30 µin/in-°F @Temperature 1110 °F |
hardened to 45 HRC |
Bohler-Uddeholm UDDEHOLM QRO® 90 SUPREME Hot Work Tool Steel Chromium-molybdenum-vanadium alloyed steelQRO® 90 SUPREME is a premium hot work die steel with high hot yield strength and very good temper resistance. Especially suited for die casting of aluminum.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 21.1 - 204 °C |
7.30 µin/in-°F @Temperature 70.0 - 400 °F |
|
Carlson C 625 Nickel-Chromium-Molybdenum Alloy General DescriptionCarlson Alloy C 625 is a nickel-chromium-molybdenum alloy that combines high strength and oxidation resistance with excellent corrosion resistance. C 625 exhibits exceptional fat.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 23.9 - 427 °C |
7.30 µin/in-°F @Temperature 75.0 - 800 °F |
|
Carlson GOC 276 Nickel-Molybdenum-Chromium General DescriptionCarlson Alloy GOC 276 is a nickel-molybdenum-chromium alloy exhibiting outstanding corrosion resistance over a wide range of service environments. This alloy is generally use in .. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 300 °C |
7.30 µin/in-°F @Temperature 77.0 - 572 °F |
|
Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Annealed 1093°C 1 hr Data provided by Carpenter Technology Corporation.Annealing followed by water quench and low stress grinding prior to tensile testing.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting h.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 300 °C |
7.30 µin/in-°F @Temperature 77.0 - 572 °F |
|
Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Annealed 1093°C 2 hr Data provided by Carpenter Technology Corporation.Annealing followed by water quench and low stress grinding prior to tensile testing.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting h.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 300 °C |
7.30 µin/in-°F @Temperature 77.0 - 572 °F |
|
Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Annealed 1121°C 1 hr Data provided by Carpenter Technology Corporation.Annealing followed by water quench and low stress grinding prior to tensile testing.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting h.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 300 °C |
7.30 µin/in-°F @Temperature 77.0 - 572 °F |
|
Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Annealed 1149°C (2100°F) 1 hr Data provided by Carpenter Technology Corporation.Annealing followed by water quench and low stress grinding prior to tensile testing.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting h.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 250 °C |
7.30 µin/in-°F @Temperature 482 °F |
|
ATI Allvac® 718Plus™ Nickel Superalloy Allvac 718Plus alloy (UNS N07818) is a precipitation hardened nickel-base material that exhibits high temperature tensile strength and stress rupture performance. This alloy is designed to have the.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 538 - 649 °C |
7.30 µin/in-°F @Temperature 1000 - 1200 °F |
|
Crucible Steel PDCQ Premium Quality High Toughness H13 Steel Crucible PDCQ™ is a premium version of H13, manufactured to exceed die casting industry specifications. PDCQ has at least 10 ft. lbs room temperature transverse toughness. Its enhanced toughness pr.. |
|||
CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 300 °C |
7.30 µin/in-°F @Temperature 77.0 - 572 °F |
|
Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Hot Worked Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur CCM Plus alloy is a.. |