Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 56.1 °C | 133 °F | ASTM D648 |
Polimeros Mexicanos Rotolene® 93835-TG Medium Density Polyethylene MDPE Copolymer with UV8 stabilizer in natural and colors.Recommended for rotomolding. Used for manufacture of water tanks > 2000 liters, cisterns, farm tanks, or tanks to contain strong acids and b.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C | 133 °F | 120°C/h; ISO 75/1 |
Polykemi AB POLYelast TPE EC88R Thermoplastic Elastomer, PP/EPDM Information provided by Polykemi AB |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C | 133 °F | |
Reliance Industries Polypropylene - Virgin Polypropylene Information provided by Reliance Industries |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C | 133 °F | ASTM D648 |
Formosa Plastics Formolene® L43840U Rotational Molding LLDPE
(discontinued **) Butene CopolymerApplications: Toys and other non-tank rotational molding applications.Formolene L43840U is a Butene Copolymer of linear low density polyethylene for toys and other non-tank rotationa.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C | 133 °F | ASTM D648 |
Formosa Plastics Formolene® L64220UT1 Rotational Molding LLDPE
(discontinued **) Hexene CopolymerApplications: Large tanks, material handling equipment and industrial rotational molding applications.Formolene L64220U is fully heat and UV stabilized.Meets all requirements of the .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C | 133 °F | ASTM D648 |
LyondellBasell Petrothene® GA694189 Linear Low Density Polyethylene, Injection Molding Grade PETROTHENE GA694189 is a pelletized LLDPE copolymer resin for injection molding. Typical applications include lids and thin-walled items that require high flow and short cycle times. GA694189 exhibi.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C | 133 °F | ISO 75 |
GEHR Plastics ECOGEHR® PLA-LF Polylactic Acid PLA-L is a blend of polylactide, lignin, lingo-cellulosic, natural fatty acids, waxes and wood fibers. This material possesses good mechanical properties similar to ABS. This bioplastic has an opera.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C | 133 °F | ASTM D648 |
LyondellBasell Astryn BB725GC Polypropylene Copolymer, Mineral Filled Key Features: medium melt flow, medium high modulus, UV-stabilized, mineral-filled polypropylene copolymer, excellent impact and stiffness balance, good processability, good weatherability,Applicati.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C | 133 °F | ASTM D648 |
Samyang Triel® 5401BM Thermoplastics Polyetherester Elastomer, Blow Molding Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5401BM is for blow molding applications.Applications: Automotive - CVJB and BellowsInformation provided .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C @Thickness 3.20 mm |
133 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 391 Ionomer DescriptionFormion® FI 391 is a non-reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low temperature ductility, and medium stiffness. Formion F1 391U i.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C @Thickness 3.20 mm |
133 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 391 Ionomer DescriptionFormion® FI 391 is a non-reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low temperature ductility, and medium stiffness. Formion F1 391U i.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C @Thickness 3.20 mm |
133 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 391 Ionomer DescriptionFormion® FI 391 is a non-reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low temperature ductility, and medium stiffness. Formion F1 391U i.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C @Thickness 3.20 mm |
133 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 391 Ionomer DescriptionFormion® FI 391 is a non-reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low temperature ductility, and medium stiffness. Formion F1 391U i.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C @Thickness 3.20 mm |
133 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 391 Ionomer DescriptionFormion® FI 391 is a non-reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low temperature ductility, and medium stiffness. Formion F1 391U i.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C @Thickness 3.20 mm |
133 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 391 Ionomer DescriptionFormion® FI 391 is a non-reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low temperature ductility, and medium stiffness. Formion F1 391U i.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 56.1 °C | 133 °F | ASTM D648 |
Aclo Accutech Polypropylene Copolymer CP0436C40L Calcium Reinforced |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C | 133 °F | ASTM-D648 |
Braskem RA34U3 LLDPE Rotomolding Polyethylene The resin RA34U3 is a linear low-density polyethylene, 1-butene based, with a good balance of processability, environmental stress cracking resistance, and impact strength. It contains long term UV6.. |