- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 156 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 156 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C @Thickness 3.18 mm |
156 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Rigid Extrusion 84110 Polyvinyl Chloride, Rigid (PVC, Rigid) Note: NSF listings are obtained on specific colors. Contact PolyOne for the latest listing of approved colors for this product. Note: The Cell Classification was determined using the notched Izod te.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | |
| Plastcom SLOVAMID 66 MI PA66, improved strength FeaturesModified with thermoplastic reactive caoutchouc, determined for mouldings with high toughness also at minus temperatures. Eligible application for ski-shoes, helmets for sport and other safe.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | 75/Method Af |
| Premix Thermoplastics PRE-ELEC® ESD 6300 Static Dissipative Thermoplastic Compound PRE-ELEC® ESD 6300 is a static dissipative thermoplastic compound based on high impact polystyrene. The dissipative property is permanent and built into the polymer chain. PRE-ELEC® ESD6300 has be.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ASTM D648 |
| Nilit Polynil® N66-P300 High Viscosity Nylon 6/6 Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | Unannealed; ASTM Data |
| Americas Styrenics Styron® 489M High Impact Polystyrene
(discontinued **) STYRON® 489M high impact polystyrene resin is a high flow resin with excellent impact. When used unmodified for the manufacture of food contact articles STYRON 489M complies with the US Food, Drug .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 13% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ISO 75-1/-2 |
| Aardvark Polymers AARTEL® 1000 Rotational Molding Resin Aartel 1000 is our premium grade of toughened impact modified acetal copolymer. Aartel 1000 is formulated with high impact properties combined with extended mechanical properties and elevated resist.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Lubricomp RL001 PA 66 LNP Lubricomp* RL001 is a Nylon 6/6 base resin containing PTFE lubricant. Characteristics are internally lubricated.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C @Thickness 3.20 mm |
156 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 7062HP PBT ENDURAN 7062HP is a 38% mineral filled & FDA compliance injection moulding resin. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-LOY A3000T ABS (Europe-Africa-Middle East) LNP* Stat-loy* A3000T is a compound based on Acrylonitrile Butadiene Styrene resin. Added features of this material include: Antistat. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ISO 75-1, 2 |
| Polyplastics Duracon® SX-35 Acetal Co-polymer (POM), Flexible, Lower noise DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ASTM D648 |
| A. Schulman POLYFLAM™ RPP 1174 Talc Filled, Homopolymer Polypropylene DescriptionPolyflam® RPP 1174 is a high performance talc filled homopolymer polypropylene product with UL V0 flammability and 105°C temperature index at 0.81 mm. RPP 1174 is non-dripping and has .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | |
| Eastman Eastapak 9921 PET ISO data as provided by the manufacturer, Eastman Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | annealed; ISO 75-1/-2 |
| DuPont Performance Polymers Crastin® CE2055 BK580 Polybutylene Terephthalate (PBT) Unreinforced Low Viscosity Polybutylene Terephthalate Crastin CE2055 is an unreinforced low viscosity polybutylene terephthalate resin for injection molding.Information provided by DuPont Performanc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | |
| Aclo Accutech Polypropylene Homopolymer HP0336M20L Mica Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ISO 75-2/AF |
| Addiplast Addilene H 490 M10S Flame Retardant Polypropylene Flame retardant, mineral filled, with halogensInformation provided by Addiplast. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ISO 75-2/A |
| Ascend Performance Materials Vydyne® 49 Nylon 66, DAM Vydyne® 49 is a general-purpose, impact-modified PA66 resin. Available in natural, it is recognized for all the processing and property advantages inherent to PA66 with the addition of improved imp.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ASTM D648 |
| Chem Polymer Chemlon 212 Nylon 6, Lubricated, GP A medium viscosity, general purpose injection molding grade nylon 6. Internally lubricated for excellent mold release properties.Data provided by the manufacturer, Chem Polymer. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | Unannealed; ISO 75-2/A |
| Ascend Performance Materials Vydyne® 49 Nylon 66, Impact Modified, DAM Vydyne® 49 is general-purpose, impact-modified PA66 resin. Available in natural, is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact s.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | Unannealed; ISO 75-2/A |
| Ascend Performance Materials Vydyne® 49H NT Nylon 66, Impact Modified, DAM Vydyne® 49H NT is general-purpose, impact-modified PA66 resin. Available in natural, it is heat-stabilized for improved resistance to elevated temperatures. The heat-stabilized for improved resista.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ASTM D648 |
| Chem Polymer Chemlon 223 Nylon 6, Nucleated A highly nucleated, lubricated nylon 6 intended for applications requiring a faster cycle time. It has increased tensile strength, rigidity, creep resistance and hardness over general purpose nylon.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 - 75.0 °C | 156 - 167 °F | ASTM D648 |
| Reliance Industries PVAXX H60 The key property of all PVAXX polymer is this product`s unique capacity to biodegrade into non-toxic residues under both aerobic and non-aerobic conditions.Information provided by Reliance Industrie.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |
| RheTech Products CC40P100-01 40% Calcium Carbonate Reinforced Polypropylene, Black Applications: Consumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B902 (UV Inhibitor Added), 13% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ISO 75 |
| Polyram RamOfin PPC343T4 Polypropylene, 20% Mineral Filled 20% Mineral filled, UV stabilized, heat stabilized polypropylene for injection molding applications.Information provided by Polyram. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||