- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 226 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 226 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | 120°C/h; ASTM D 648 |
| Polimeri Europa Sinkral® C 442 ABS Resin Sinkral C 442 is a heat resistant injection molding grade offering good flow and impact resistance together with excellent thermal stability during processing. Designation: Thermoplastic ISO 2580-AB.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycoloy® CX5640 PC+ABS (Asia Pacific) Cycoloy* CX5640 is a all purpose PC+ABS blend specially developed for applications requiring weld line strength. High heat resistance combined with good flow, excellent impact and low temperature du.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CX5640 PC+ABS (Asia Pacific) Cycoloy* CX5640 is a all purpose PC+ABS blend specially developed for applications requiring weld line strength. High heat resistance combined with good flow, excellent impact and low temperature du.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycoloy® CX5640 PC+ABS (Europe-Africa-Middle East) Cycoloy* CX5640 is a all purpose PC+ABS blend specially developed for applications requiring weld line strength. High heat resistance combined with good flow, excellent impact and low temperature du.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Cycoloy® FXC630ME PC+ABS (Asia Pacific) PC+ABS, ECO-conforming flame retardant with metallic or pearlescent appearance. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Cycoloy® FXC810AR PC+ABS (Europe-Africa-Middle East) CYCOLOY FXC810AR is a multi-purpose PC+ABS injection moulding grade, suitable for those applications that require Ares colour effects. The colour package may effect performance.This data was supplie.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Cycoloy® FXC813SK PC+ABS (Europe-Africa-Middle East) CYCOLOY FXC813SK is a multi purpose PC+ABS injection moulding grade, providing a favourable balance of engineering properties. CYCOLOY FXC813SK is suitable for those applications that require sparkl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® ADX1016R PC (Europe-Africa-Middle East) Lexan Copolymer resin with improved chemical resistance, available only in limited colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Cycoloy® C1200HF PC+ABS (Europe-Africa-Middle East) CYCOLOY C1200HF is the improved version of CYCOLOY C1200 and has been developed to provide enhanced productivity and surface appearance for |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Not Annealed; ASTM D648 |
| DuPont Performance Polymers Delrin® 500AL NC010 Acetal Homopolymer
(Unverified Data**) Delrin® 500AL is a medium viscosity acetal homopolymer, with an advanced system of lubrication for applications requiring low wear and/or coefficient of friction against steel, itself or other plas.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® SLDM310 PC (Asia Pacific) Mineral filled Antistatic Polycarbonate, HDT110degC type |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 6.40 mm |
226 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa MAC-601 DY Modified 60/40 PC/ABS Alloy Features:Excellent balance propertiesHigh impact strengthGood electro-plating propertiesGood processing propertiesApplications:Injection moldingAutomobile instrument panelPower toolComputer and acce.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 3.17 mm |
226 °F @Thickness 0.125 in |
ASTM D648 |
| Metton LMR M1534 Liquid Molding Resin Different product numbers represent different formulations for customer specific needs such as liquid freezing point. Metton LMR is a tough and durable engineering plastic material used to produce .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | ISO 75-1,-2 |
| Ineos ABS Lustran® Ultra 4115 ABS Pellets (a-methylstyrene-SAN / PC-modified), Very High Heat Grade Lustran® Ultra 4115 is very high heat grade with high impact resistance and is PC-modified. It is used for the production of molded plastic articles. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP OL003A PPS - Branched LNP* LUBRICOMP* OL003A is a compound based on PPS - Branched resin containing 15% PTFE. Added features of this grade are: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Unannealed; ASTM D648 |
| Techmer ES Electrablend® PEI 04008 MB Availability: North AmericaForms: PelletsFeatures: Conductive and CopolymerInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON KD000 Acetal Copolymer (Europe-Africa-Middle East) LNP STAT-KON KD000* is also know as: LNP STAT-KON K, LNP STAT-KON KXC. It is a compound based on Acetal resin containing Carbon Powder. Added features of this material include: Electrically Conduct.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics XYLEX X7509HP PC+POLYESTER PC+Polyester alloy. Houseware applications. USA/Europe Food contact. this grade will no longer be supported with biocompatibility information and should not be used for medical applications which r.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® POM CO X MB Acetal Availability: North AmericaForms: PelletsAdditive: LubricantFeatures: Lubricated, Good Wear Resistance, Low Friction and CopolymerUL File Number: E157318Information provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® POM CO UV Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: CopolymerInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Unannealed; ASTM D648 |
| Techmer ES Statiblend® PBT 03003 Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass FiberFeatures: Conductive, Antistatic and ESD ProtectionInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Unannealed; ASTM D648 |
| Techmer ES Statiblend® PBT GF10 SS5 MB Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 10% Filler by WeightAdditive: AntistaticFeatures: Conductive, Antistatic and ESD ProtectionInformation provided by TP Comp.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOTUF MF004AI PP LNP* Thermotuf* MF004AI is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: High Impact. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL BN9003G PPE+HIPS PPE+PS blend. Unfilled. Blow molding. Excellent balance of impact and surface aesthetics. Suitable for automotive exterior components including spoilers. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl CRX2201 PPE+HIPS (Asia Pacific) Noryl* CRX2201 resin is a 25% mineral reinforced, injection moldable modified polyphenylene ether resin designed for improved chemical resistance when compared with standard Noryl resins. Noryl CRX.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | |
| Covestro Bayblend® T 84 Polycarbonate/ABS Blend Easier flowing than BAYBLEND T 85 MN.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron IMG1130 Glass Reinforced Grade Glass Reinforced ABS & SAN Resins for product specific requirement of very high rigidity and temperatureInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | ISO Data |
| BASF Capron® 8260 HS BK-102 40% Mineral-Filled Nylon 6 (Dry)
(discontinued **) Capron 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced nylon 6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl CRX2201 PPE+HIPS (Europe-Africa-Middle East) Noryl* CRX2201 resin is a 25% mineral reinforced, injection moldable modified polyphenylene ether resin designed for improved chemical resistance when compared with standard Noryl resins. Noryl CRX.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 911DP NC010 Acetal Homopolymer
(Unverified Data**) Delrin® 911DP is a low viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage, less shrinkage, fewer voids).Information provided by.. |
|||