- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 235 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 235 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C @Thickness 3.20 mm |
455 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics EXTEM XH1005 TPI Resin Thermoplastic Polyimide Extem* XH1005 Resin. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C @Thickness 3.20 mm |
455 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics EXTEM XH1015 TPI Resin (Asia Pacific) Thermoplastic Polyimide Extem* XH1015 Resin. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C @Thickness 3.20 mm |
455 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics EXTEM XH1015 TPI Resin (Europe-Africa-Middle East) Thermoplastic Polyimide Extem* XH1015 Resin. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C @Thickness 3.20 mm |
455 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics EXTEM XH1015F TPI Resin (Europe-Africa-Middle East) Thermoplastic Polyimide Extem* XH1015 Resin. EFSA food Contact approved. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | 120°C/h; ISO 75/1 |
| Polykemi AB SCANAMID 66 A33^E F15 Nylon 66, Glass Fiber Reinforced, Modified Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75 |
| Nilit FRIANYL A63 TF-KV 1530 Nylon 6.6 for injection molding, 15% PTFE lubricated and 30% glass ball reinforced Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1, -2 |
| Celanese Celstran® PA66-GF50-0112P7,5/10 PA666, 50% Glass Reinforced
(Unverified Data**) Material code according to ISO 1043-1: PA66PA66/6 copolymer with 50% ash content high gloss, UV stabilized, UL - listing (f1)Information provided by Celanese |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | |
| Idemitsu Kosan Xarec® WA 552 SPS, 30% Glass Filled Crystalline Polymer, Glass Filled/Impact Modified. Used in Automotive and Industrial applications. NSF and medical approval ISO 10993 |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF30 RM-1 L 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: LubricantFeatures: Lubricated and Low Moisture AbsorptionInformation provided .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C @Thickness 3.20 mm |
455 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Thermocomp OF002A PPS LNP* Thermocomp* OF002A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C @Thickness 3.20 mm |
455 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOTUF VF006U Super Tough Nylon LNP* Thermotuf* VF006U is a compound based on Super Tough Nylon containing Glass Fiber. Characteristics of this grade are High Impact. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ASTM D648 |
| Chase Plastics CP Pryme® NN213GL (DAM) Nylon 66, 13% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ASTM D648 |
| A. Schulman ComAlloy® E-14292 Hi-Flow Glass Reinforced PPS Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
| DSM Akulon® S223-G4U (Dry) 23% Glass Reinforced Nylon 66 (North America) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
| DSM Arnite® AV2 370 XL-T PET-GF35 35% Glass Reinforced, Low Outgassing, Thermal conductive material |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® GV-6 FWA nat PA*-GF60 Product description: Grivory GV-6 FWA natural is a 60% glass fiber reinforced engineering thermoplastic material based on a combination of semicrystalline Polyamide with partially aromatic copolyami.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® GV-6H EF black 9915 PA*-GF60 Product description: Grivory GV-6H black 9915 is a 60% glass fiber reinforced engineering thermoplastic material based on a combination of semicrystalline Polyamide with partially aromatic copolyami.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® TSG-30/4 FA PA666-GF30 Information provided by EMS Grivory |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® TSG-30/4 V0 PA666-GF30 FR Product description: Grilon TSG-30/4 V0 is a heat stabilized, flame retardant, self-extinguishing engineering thermoplastic, reinforced with glass-fiber 30% (by weight) based on a semi-crystalline P.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Star L PA66 30V D61 PA66, Glass Fiber Filled, Injection Molded Star L PA66 30V D31 is a PTFE/Silicone Lubricated, Glass Fiber Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Eurostar Staramide RF00AES PA66/6, 50% Glass Filled, Injection Molded Staramide RF00AES is a 50% Glass Fiber Reinforced Polyamide 66/Polyamide 6 Injection Molding Resin (also known as Staramide 66 C 50V S3)Information provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1, -2 |
| Celanese THERMX CG923 PCT, 20% Glass Reinforced Thermx« CG923 is a 20% glass fiber reinforced and flame retardant polycyclohexylenedimethylene terephthalate for injection molding.Information provided by Celanese |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1, -2 |
| Celanese VECTRA® 2310MT 30% Glass Filled, Medical Grade Liquid Crystal Polymer (LCP) Description: 30% Glass Reinforced medical grade with improved strength stiffness over 1310MT. Has established Drug and Device Master Files.Information provided by Celanese Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1, -2 |
| Celanese VECTRA® E530i 30% Mineral Reinforced Liquid Crystal Polymer (LCP) Description: Very easy flowing grade with very good heat resistance, good mechanical properties, platable and good impact strength. 30% mineral reinforced.Information provided by Celanese Corporatio.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ASTM D648 |
| A. Schulman ComAlloy Voloy® 686 Nylon 6/6, Glass Fiber/Bead Reinforced, Nylon 6/6 Alloy, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.45% Glass Fiber/Bead Reinforced. Halogen- and phosphorous-freeThe ComAlloy product line has been integrated into the A Schulman prod.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | DIN 53461 |
| Polyram PlusTek RA320G6 Nylon 6.6, 30% Glass Fiber, Flame Retardant 30% glass fiber reinforced, flame retardant polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ASTM D 648 |
| RTP Company RTP 3499-3 X 113393 A Liquid Crystal Polymer (LCP), Glass Fiber - LDS Platable Dielectric Constant K: 4.18 at 1 GHz, 4.02 at 3 GHz, 4.04 at 5 GHz Dissipation factor DF: 0.0067 at 1 GHz, 0.0059 at 3 GHz, 0.0056 at 5 GHz |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 235 °C | >= 455 °F | ASTM D648-61 |
| Budd DSM-949, Diesel Grade SMC, Vinyl Ester, Black
(discontinued **) Used for parts requiring high strength at room temperature, good retention of properties at high temperatures and corrosion resistance, such as diesel engine external body parts.Data provided by the.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | DIN 53461; ASTM D648 |
| Kolon KOPA® KN3321G15VO G/F Reinforced & Flame Retardant Nylon 66 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstanding .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1, -2 |
| Celanese VECTRA A130 LCP, 30% Glass Reinforced The Standard for the Industry. Excellent balance of properties, including easy flow, easy processing, thermal stability, chemical resistance, mechanical and electrical properties. Suitable for vapo.. |
|||