- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 380 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 380 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | ASTM D648 |
| Oxford Polymers 10GF 10% Glass Fiber Reinforced Polyetherimide/Polycarbonate Alloy 10% Glass Fiber Reinforced Polyetherimide/Polycarbonate AlloyInformation provided by Oxford Polymers. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | ASTM D648 |
| Oxford Polymers OPX782 Polybutylene Terephthalate (PBT), Impact Modified/ Glass Beads Polybutylene Terephthalate (PBT), Impact Modified/ Glass BeadsInformation provided by Oxford Polymers. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | ASTM D648 |
| Niche Polymer PA6GF13N Nylon 6, 13% Glass Fiber Filled Information provided by Niche Polymer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | ASTM D648 |
| Polymer Resources NY66-M40 Nylon 66, 40% Mineral Filled Nylon 66, 40% Mineral Filled, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | ASTM D648 |
| Polymer Resources NY66-M40-[color]-H Nylon 66, 40% Mineral Filled, Heat Stabilized Nylon 66, 40% Mineral Filled, Lubricated, Heat StabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | ASTM D648 |
| Polymer Resources TP-HG40 Polybutylene Terephthalate, 40% Glass Reinforced Alloy Polybutylene Terephthalate, 40% Glass Reinforced AlloyProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informatio.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylon® N1040MHL Nylon 6/6 (DAM) Information provided by Ravago. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | ASTM D648 |
| Polymer Resources NY66-M40-[color]H Nylon, 40% Mineral Filled, Lubricated, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 GF15 IM HS L 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impac.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 GF15 IM L 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impac.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 GF15 IM1 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impac.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 GF18 IM 511 18% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 18% Filler by WeightAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impac.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 GF20 IM2 BK 20% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impac.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® PBT GF30 FR-S AS 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: AntistaticFeatures: Flame Retardant, Antistatic and Non-BloomingProcessing Method: Injection.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® TPX-PBT-00014 40% Glass/Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral, 40% Filler by WeightFeatures: Flame RetardantUL File Number: E157318Information provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 GF20 IM2 L 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightAdditive: Impact Modifier and LubricantFeatures: Impact Modified and LubricatedTPCI# 633.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GF15 15% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GF15 15% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 380 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GF15 15% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||