- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 485 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 485 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
| Oxford Polymers Oxnilon 66-43GF 43% Glass Fiber Filled Nylon 66 for Injection Molding 43% Glass Fiber Filled Nylon 66 for Injection MoldingInformation provided by Oxford Polymers. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
| Polymer Resources NY66-G43 Nylon 66, 43% Glass Reinforced Nylon 66, 43% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are test.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
| Polymer Resources NY66-G43-[color]-H Nylon 66, 43% Glass Reinforced, Heat Stabilized Nylon 66, 43% Glass Reinforced, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
| Techmer ES Electrafil® J-1/CF/30/TF/13/SI/2 Nylon 66, 30% Carbon Fiber, 13% PTFE, 2% Silicone |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® PA6/6 GF33 FR-N BK 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightFeatures: Flame Retardant and Halogen FreeAppearance: BlackInformation provided by TP Composites, Inc... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF33 RM L 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated, Low Moisture Absorption and.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 CF10 TL15 BK 10% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 10% Filler by WeightAdditive: PTFE + Silicone Lubricant(15%)Features: Lubricated and Good Wear ResistanceAppearance: Blac.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 CF20 TL15 BK 20% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 20% Filler by WeightAdditive: PTFE Lubricant(15%) Features: Lubricated, Good Wear Resistance and Low Friction Appearance:.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 CF30 TL12 BK 30% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE Lubricant(15%) and Silicone LubricantFeatures: Lubricated, Good Wear Resistance and Lo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 CF30 TS15 BK 30% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE Lubricant(15%) and Silicone LubricantFeatures: Lubricated, Low Friction and Good Wear .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
| Techmer ES Plaslube® J-1/30/SI/2 Nylon 66, 30% GFR, 2% Silicone Plaslube silicone lubricated nylon 66 grades are cost-effective wear and friction materials with low coefficients of friction. These grades have a potential for noise reduction due to the migratory.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® PA6/6 GF25 FR-N IM3 25% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 25% Filler by WeightAdditive: Impact ModifierFeatures: Flame Retardant and Impact ModifiedAppearance: RedInformation provi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF40H 40% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
| Chase Plastics CP Pryme® NN130GMD2 (COND, 50% RH) Nylon 66, 30% Glass Fiber Reinforced, 2% MoS2 Lubricated Information provided by Chase Plastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
| Chase Plastics CP Pryme® NN130GMD2HS (COND, 50% RH) Nylon 66, 30% Glass Fiber Reinforced, 2% MoS2 Lubricated, Heat Stabilized Information provided by Chase Plastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
| Chase Plastics CP Pryme® NN130GMD2HS (DAM) Nylon 66, 30% Glass Fiber Reinforced, 2% MoS2 Lubricated, Heat Stabilized Information provided by Chase Plastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
| Chase Plastics CP Pryme® NN143GL (DAM) Nylon 66, 43% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF40H 40% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF40H 40% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF40H 40% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF40H 40% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 485 °F | ASTM D648 |
| Quantum Nylon 6/6 30% Glass Fiber Filled Information provided by Quantum Advanced Engineering Plastics |
|||