- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 86.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 86.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ISO 75-2 |
| Polycasa PS QUINN PS sheets have good optical properties and a brilliant surface. The QUINN PS range contains sheets that are easy to fabricate, to vacuum form, and show a high light transmission (min 88% wavel.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycolac® S708C ABS (Europe-Africa-Middle East) Cycolac* S708C is an improved scratch resistant ABS product with high stiffness and heat, used for applications in appliances, telecom, business machines and TV industries.This data was supplied by .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP FARADEX AS004 ABS (Europe-Africa-Middle East) LNP* Faradex* AS004 is a compound based on Acrylonitrile Butadiene Styrene resin containing Stainless Steel Fiber. Added features of this material include: EMI/RFI Shielding. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP AI001XXH ABS LNP* Lubricomp* AI001XXH is a compound based on ABS containing 2% Silicone. Characteristics of this grade are: Healthcare and Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycolac® INP581 ABS+SAN High flow, low molecular weight SAN. Can be used as compounding additives for polymer blends. Can be blended with high rubber graft modifier resins to produce customized ABS properties. Suitable for.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycoloy® EFX830ME PC (Asia Pacific) Modified PC blend offering metallic look with minimal flow lines, flame retarded without using Chlorinated or Brominated additives.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ASTM D648 |
| Ineos Nova Zyntar® F7120 Developmental Flame Retardant Polystyrene
(discontinued **) Features: High flow for thin wall partsGood balance of physical propertiesUL94 V-0 @ 1.5 mm for black color Good aesthetics for injection molding Applications:Large television cabinetsConsumer elect.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ASTM D648 |
| LG Chemical HI855M PMMA, Impact Resistant Grade Molding granule designed for greater impact strength combined with the outstanding properties of conventional acrylic materialsFeatures: Excellent transparency and eleganceWeather resistance and che.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 6.40 mm |
187 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical PI641 ABS, High Impact Feature: Extrusion Molding, General Purpose, High ImpactApplication: Pipe FittingCAS No. 9003-56-9Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 6.40 mm |
187 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical PI642G ABS, General Purpose, High Modulus Feature: Extrusion Molding, General Purpose, High ModulusApplication: Pipe fittingCAS No. 9003-56-9Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 6.40 mm |
187 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical RS656H ABS, Chemical Resistance to Cyclopentane Feature: Extrusion Molding, General Purpose, Chemical Resistance to CyclopentaneApplication: Refrigerator Inner LinerCAS No. 9003-56-9Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ASTM D648 |
| Lucite International XL Sanitary Ware Acrylic Sheet Lucite® XL continuous-cast cross-linked acrylic sheet is specially formulated for deep-draw thermoforming. It is used primarily for production of spas.Benefits: Smooth surface; Infinite colors an.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ISO 75 |
| Styrolution Luran® HD 20 SAN Luran HD 20 is an easy-flow grade of SAN especially designed for the medical market. It is suitable for moldings with very thin walls and / or adverse flow length to wall ratio. It features very goo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 6.40 mm |
187 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® LX-0987EXS ABS, Unreinforced Metallic-Look Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 6.40 mm |
187 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® LX-0989EXS ABS, Unreinforced Metallic-Look Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 6.40 mm |
187 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® PT-0180 ABS, Unreinforced Painting Grade Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 6.35 mm |
187 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Samsung Cheil Industries Infino® PCA-NH1015V Flame Retardant |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP PH0320A PA 6 (Asia Pacific) LNP THERMOCOMP* PH0320A is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 6.40 mm |
187 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL N850 PPE+PS ECO-FLO(tm). ECO conforming, nonhalogenated flame retardant PPE+PS. High flow. Electrical and Business Equipment applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ISO 75 |
| Styrolution PS 158K GPPS Styrolution PS 158K is a heat resistant, rapid freezing general purpose grade. It is suitable for expanded sheet and film; for blends with high impact Styrolution PS in heat contact applications; fo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | 0.5 inch; ASTM D648 |
| PlastxWorld CEVIAN® E80 ABS Inherently Static Dissipative Transparent ABSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | unannealed; ISO 75 |
| Chi Mei Kibisan® PN-106 L150 SAN High Clarity |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Starflam A28UL PA66, Flame Retardant, Injection Molding Staramide A28UL is Unfilled, Halogen Free and Red Phosphorous Free, Flame Retardant Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | unannealed; ISO 75 |
| Chi Mei Polylac® PA-763 ABS - Flame Retardant F.R. High Heat Weather Resistant |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ASTM D648 |
| ALM PA 250 Nylon 12 SLS Prototyping Polymer Highly Recyclable Nylon 12 Laser Sintering Material.Engineered for excellent mechanical properties, part definition and surface finish. Stabilized against thermal degradation resulting in little or.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | |
| BASF Polystyrol® 168 N Polystyrene (Europe) High molecular, heat-resistant grades used where high strength is required. Suitable for expanded film.Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | |
| BASF Polystyrol® 168 NO Polystyrene (Europe) High molecular, heat-resistant grades for the extrusion of low-taint food packaging, especially BOPS.Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ASTM D648 |
| ALM PA 606-FR Filled Nylon 12 Prototyping Polymer Only commercially available fire retardant nylon 12 material, which meets FAR 25.853 60 second burn specification.The parts produced from PA 606-FR have a much smoother surface finish and sharper fe.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ISO 75-1/-2 |
| Styrolution Luran® 348 Q Crystal Clear Transparent 77850 SAN Description: Highly transparent grade with low natural color.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | 0.5 inch; ASTM D648 |
| PlastxWorld CEVIAN®-V T150 ABS Medium impact transparent ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||