- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 94.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 94.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ASTM D648 |
| Plaskolite West Optix® CA-82 UVA UV-Absorbing Acrylic Resin Special UV-absorption grade, extrusion and injection moldingApplications: A special UV-absorption acrylic resin for injection molding and contains a mold release agent. This resin offers high heat .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | |
| Ineos ABS Lustran® QE 1045 A, Injection Grade
(discontinued **) Injection molding grade, high modulus, only available in black.Applications: For automotive application.Information provided by Bayer.LANXESS was spun-off from Bayer in early 2005. Business renamed.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Annealed, 80°C, 4 hours; ISO 175 |
| LG Chemical HI-121 ABS, High Impact Feature: Injection Molding, Well Balanced Mechanical PropertiesApplication: Electric & Electronic Products, Miscellaneous GoodsCAS No. 9003-56-9Information Provided by LG Chem |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Annealed, 80°C, 4 hours; ISO 175 |
| LG Chemical HI-151 ABS, Middle Impact Information Provided by LG Chem |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | |
| Ineos ABS Lustran® M202AS Grade for self coloring, optimized base color, easy flowing, contains antistatic additives. ,Property data per ISO test methods. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ASTM D648 |
| Ineos Nova 1600 High Heat Crystal Polystyrene High heat resistance, Moderate flow, Good balance of strength and set-upApplications: Foam extrusion, Injection moldingExposure to gamma radiation in the 2.02-6.06 megarad range has no significant e.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Annealed, 80°C, 4 hours; ISO 175 |
| LG Chemical NS-161 ABS, Antistatic, High Strength Information Provided by LG Chem |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Annealed, 80°C, 4 hours; ISO 175 |
| LG Chemical NT-520 ABS, High Flow, Non Toxic Information Provided by LG Chem |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ASTM D648 |
| Ineos Styrenics Polystyrene 168M (NAFTA) High heat, high molecular weight general purpose polystyrene with low crystal clarity. It offers high stiffness for extrusion/thermoforming applications, especially for the food packaging.Informati.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | |
| Ineos Styrenics Polystyrene 168M0 (NAFTA) High heat, high molecular weight general purpose polystyrene with low residual volatiles. It is ideally suited for use in critical low taste, low odor food packaging products.Information provided b.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Lubriloy D20001 PC LNP LUBRILOY* D20001 is a compound based on Polycarbonate resin containing Flame Retardant, Proprietary Lubricant. Added features of this material include: Flame Retardant.This data was supplied by.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Xenoy® IQ4840 PBT+PC (Asia Pacific) Xenoy iQ4840 (PBT+PC) resin is an environmental responsible, sustainable, and low carbon footprint resin. It is a 10% mineral filled resin with high modulus and ductile (HMD) characteristics. Xen.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Xenoy® IQ4840 PBT+PC (Europe-Africa-Middle East) Xenoy iQ4840 (PBT+PC) resin is an environmental responsible, sustainable, and low carbon footprint resin. It is a 10% mineral filled resin with high modulus and ductile (HMD) characteristics. Xen.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ISO 75 |
| Styrolution Novodur® E401 ABS Novodur E401 is a high impact extrusion grade with good surface appearanceInformation provided by Styrolution |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ISO 75 |
| Styrolution Terluran® GP-35 ABS Terluran GP-35 is a very high flow grade of ABS for injection molding with good resistance to impact and heat deflection.Information provided by STYROLUTION, which is a joint venture between BASF an.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp RX06324 PA 66 (Asia Pacific) This material is Mineral filled Nylon grade with high dielectric constantThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | 0.5 inch unannealed; ASTM D648 |
| PlastxWorld CEVIAN® SERG1 10% GF ABS Glass fiber reinforced and flame retarded ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ASTM D648 |
| A. Schulman POLYPUR™ FPU 1156 Thermoplastic Polyurethane Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | annealed; ISO 75 |
| Chi Mei Kibilac® PW-957 ASA Polymer Injection |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 127UVE RD402 Acetal (POM)
(Unverified Data**) UV Stabilized High Viscosity Acetal Homopolymer with Very Low Emissions Delrin 127UVE RD402 (formerly DE20555) is a high viscosity acetal homopolymer with UV stabilizers pigmented red with very low .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ISO 75-1,-2 |
| Covestro Bayblend® FR410 MT Rubber Modified PC Blend, 10% Mineral Filled Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Rubber modified PC blend.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron SE-32M ABS Sheet Extrusion Grade Super high and Very High Impact Sheeting grades for Automobile & Luggage ApplicationsInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron HI-34 ABS High Impact Injection Molding Very High & Medium Impact, Paintable Automotive Grades Information provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron SE-22 ABS Sheet Extrusion Grade Sheet Extrusion grade for profile & DoorsInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron SE-32M ABS Sheet Extrusion Grade Super high and Very High Impact Sheeting grades for Automobile & Luggage ApplicationsInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron SE-20P ABS Sheet Extrusion Grade ABS Pipe GradeInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron HI-40 B ABS High Impact Injection Molding Very High & Medium Impact, Paintable Automotive Grades Information provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron IM-11B ABS Injection Molding Grade High Impact Strength, Medium Flow, High Fatigue ResistanceInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ASTM D648 |
| Styrolution NAS® 21 Acrylic Copolymer Features:Sparkling clarity Scratch resistant Can be blended with K-Resin at any level to modify flexibility, surface hardness, heat distortion temperatures, etc. Styrenic processing advantages Gamma.. |
|||