Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 22.5 µm/m-°C @Temperature 20.0 - 1000 °C |
12.5 µin/in-°F @Temperature 68.0 - 1830 °F |
|
Goodfellow Dural® Aluminum /Copper/Magnesium Alloy High strength, low weight alloy; in the solution heat-treated and aged condition, mechanical properties are as good as, or better than, low-carbon steel. Limited weldability. Used in aircraft and ae.. |
|||
CTE, linear | 22.5 µm/m-°C @Temperature 20.0 - 100 °C |
12.5 µin/in-°F @Temperature 68.0 - 212 °F |
|
Aleris Weldural Aluminum Alloy, 400 mm Thickness Sample treatment not specified for property data.Applications include precise mechanical parts with high dimensional stability, machine components, molds, and refrigeration engineering. Good weldab.. |
|||
CTE, linear | 22.5 µm/m-°C @Temperature 20.0 - 100 °C |
12.5 µin/in-°F @Temperature 68.0 - 212 °F |
|
Aleris Weldural Aluminum Alloy, 600 mm Thickness Sample treatment not specified for property data.Applications include precise mechanical parts with high dimensional stability, machine components, molds, and refrigeration engineering. Good weldab.. |
|||
CTE, linear | 22.5 µm/m-°C @Temperature 20.0 - 100 °C |
12.5 µin/in-°F @Temperature 68.0 - 212 °F |
|
Aleris Weldural Aluminum Alloy, 100 mm Thickness Sample treatment not specified for property data.Applications include precise mechanical parts with high dimensional stability, machine components, molds, and refrigeration engineering. Good weldab.. |
|||
CTE, linear | 22.5 µm/m-°C @Temperature 20.0 - 100 °C |
12.5 µin/in-°F @Temperature 68.0 - 212 °F |
|
Aleris Weldural Aluminum Alloy, 200 mm Thickness Sample treatment not specified for property data.Applications include precise mechanical parts with high dimensional stability, machine components, molds, and refrigeration engineering. Good weldab.. |
|||
CTE, linear | 22.5 µm/m-°C @Temperature 20.0 - 100 °C |
12.5 µin/in-°F @Temperature 68.0 - 212 °F |
|
Aleris Weldural Aluminum Alloy, 300 mm Thickness Sample treatment not specified for property data.Applications include precise mechanical parts with high dimensional stability, machine components, molds, and refrigeration engineering. Good weldab.. |
|||
CTE, linear | 22.5 µm/m-°C @Temperature 20.0 - 100 °C |
12.5 µin/in-°F @Temperature 68.0 - 212 °F |
|
Aleris Weldural Aluminum Alloy, 500 mm Thickness Sample treatment not specified for property data.Applications include precise mechanical parts with high dimensional stability, machine components, molds, and refrigeration engineering. Good weldab.. |
|||
CTE, linear | 22.5 µm/m-°C @Temperature 20.0 - 100 °C |
12.5 µin/in-°F @Temperature 68.0 - 212 °F |
|
Aleris Weldural Aluminum Alloy, 700 mm Thickness Sample treatment not specified for property data.Applications include precise mechanical parts with high dimensional stability, machine components, molds, and refrigeration engineering. Good weldab.. |