Polymer Property : Thermal Conductivity = 255 BTU-in/hr-ftÂ²-Â°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English
Thermal Conductivity	36.7 W/m-K @Temperature 1200 Â°C	255 BTU-in/hr-ftÂ²-Â°F @Temperature 2190 Â°F
Haynes 214Â® alloy sheet Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	36.7 W/m-K @Temperature 1200 Â°C	255 BTU-in/hr-ftÂ²-Â°F @Temperature 2190 Â°F
Haynes 214Â® alloy, sheet, 100 hours exposure at 760Â°C (1400Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	36.7 W/m-K @Temperature 1200 Â°C	255 BTU-in/hr-ftÂ²-Â°F @Temperature 2190 Â°F
Haynes 214Â® alloy, sheet, 100 hours exposure at 870Â°C (1600Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	36.7 W/m-K @Temperature 1200 Â°C	255 BTU-in/hr-ftÂ²-Â°F @Temperature 2190 Â°F
Haynes 214Â® alloy, sheet, 100 hours exposure at 980Â°C (1800Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	36.7 W/m-K @Temperature 1200 Â°C	255 BTU-in/hr-ftÂ²-Â°F @Temperature 2190 Â°F
Haynes 214Â® alloy, sheet, 1000 hours exposure at 760Â°C (1400Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	36.7 W/m-K @Temperature 1200 Â°C	255 BTU-in/hr-ftÂ²-Â°F @Temperature 2190 Â°F
Haynes 214Â® alloy, sheet, 1000 hours exposure at 870Â°C (1600Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	36.7 W/m-K @Temperature 1200 Â°C	255 BTU-in/hr-ftÂ²-Â°F @Temperature 2190 Â°F
Haynes 214Â® alloy, sheet, 1000 hours exposure at 980Â°C (1800Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	36.7 W/m-K @Temperature 1200 Â°C	255 BTU-in/hr-ftÂ²-Â°F @Temperature 2190 Â°F
Haynes 214Â® alloy, sheet, 32 hours exposure at 760Â°C (1400Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	36.7 W/m-K @Temperature 1200 Â°C	255 BTU-in/hr-ftÂ²-Â°F @Temperature 2190 Â°F
Haynes 214Â® alloy, sheet, 32 hours exposure at 870Â°C (1600Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	36.7 W/m-K @Temperature 1200 Â°C	255 BTU-in/hr-ftÂ²-Â°F @Temperature 2190 Â°F
Haynes 214Â® alloy, sheet, 32 hours exposure at 980Â°C (1800Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..