Thermal Properties | Metric | English | Comments |
---|---|---|---|
Vicat Softening Point | 210 °C @Load 0.999 kg |
410 °F @Load 2.20 lb |
120°C/min; ASTM D1525/A, ISO 306/A |
EPICHEM Epinyl PA 6 GF 30 ATP Polyamide 6, 30% Glass Characteristics: medium viscosity, 30% glass fibre, good toughness |
|||
Vicat Softening Point | 210 °C @Load 0.999 kg |
410 °F @Load 2.20 lb |
120°C/min; ASTM D1525/A, ISO 306/A |
EPICHEM Epinyl PA 6 GF 30 H Polyamide 6, 30% Glass, Heat Stabilized Characteristics: medium viscosity, 30% glass fibre, heat stabilized |
|||
Vicat Softening Point | 210 °C @Load 0.999 kg |
410 °F @Load 2.20 lb |
120°C/min; ASTM D1525/A, ISO 306/A |
EPICHEM Epinyl PA 6 GF 30 Polyamide 6, 30% Glass Characteristics: medium viscosity, 30% glass fibre, excellent mechanical properties |
|||
Vicat Softening Point | 210 °C @Load 5.00 kg |
410 °F @Load 11.0 lb |
120°C/min; ASTM D1525/B, ISO 306/B |
EPICHEM Epiter PBT GF 20 Polybutylene Terephthalate, 20% Glass Characteristics: 20% glass fibre filled |
|||
Vicat Softening Point | 210 °C @Load 5.00 kg |
410 °F @Load 11.0 lb |
120°C/min; ASTM D1525/B, ISO 306/B |
EPICHEM Epiter PBT GF 30 Polybutylene Terephthalate, 30% Glass Characteristics: 30% glass fibre filled |
|||
Vicat Softening Point | 210 °C @Load 0.999 kg |
410 °F @Load 2.20 lb |
120°C/min; ASTM D1525/A, ISO 306/A |
EPICHEM PA 6 GF 30 Polyamide 6, 30% Glass Characteristics: medium viscosity, 30% glass fibre filled |
|||
Vicat Softening Point | 210 °C @Load 5.10 kg |
410 °F @Load 11.2 lb |
dry; ISO 306 |
Azoty Tarnow™ Tarnamid® T-27 GF10 MX10 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grade, reinforced with 10% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning, good surface quality.T.. |
|||
Vicat Softening Point | 210 °C @Load 5.10 kg |
410 °F @Load 11.2 lb |
dry; ISO 306 |
Azoty Tarnow™ Tarnamid® T-27 GF30 I Polyamide 6 - Glass Fiber Reinforced 30% Glass fiber reinforced, impact modified, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following mai.. |
|||
Vicat Softening Point | 210 °C @Load 5.10 kg |
410 °F @Load 11.2 lb |
dry; ISO 306 |
Azoty Tarnow™ Tarnamid® T-27 GF25 FRV0 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grades, flammability class V0, reinforced with 25% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning.. |