Polymer Property : Thermal Conductivity = 153 BTU-in/hr-ftÂ²-Â°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Thermal Conductivity	22.0 W/m-K @Temperature 704 Â°C	153 BTU-in/hr-ftÂ²-Â°F @Temperature 1300 Â°F
Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, aged 16 hours at 760Â°C (1400Â°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	22.0 W/m-K @Temperature 704 Â°C	153 BTU-in/hr-ftÂ²-Â°F @Temperature 1300 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, aged 16 hours at 760Â°C (1400Â°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	22.0 W/m-K @Temperature <=20.0 °C	153 BTU-in/hr-ft²-°F @Temperature <=68.0 °F
CLAL-MSX ARCAP Anticorrosion AP1 0 Annealed, Drawn Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. Its machineability is one of the best of all of the corrosion resistant alloys. The very good machineability of..
Thermal Conductivity	22.0 W/m-K @Temperature <=20.0 °C	153 BTU-in/hr-ft²-°F @Temperature <=68.0 °F
CLAL-MSX ARCAP Anticorrosion AP1 H12 1/2 hard, Drawn Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin..
Thermal Conductivity	22.0 W/m-K @Temperature <=20.0 °C	153 BTU-in/hr-ft²-°F @Temperature <=68.0 °F
CLAL-MSX ARCAP Anticorrosion AP1 H14 4/4 hard, Rolled Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin..
Thermal Conductivity	22.0 W/m-K @Temperature <=20.0 °C	153 BTU-in/hr-ft²-°F @Temperature <=68.0 °F
CLAL-MSX ARCAP Anticorrosion AP1C 0 Annealed, Drawn Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un..
Thermal Conductivity	22.0 W/m-K @Temperature <=20.0 °C	153 BTU-in/hr-ft²-°F @Temperature <=68.0 °F
CLAL-MSX ARCAP Anticorrosion AP1C H13 3/4 hard, Drawn Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un..
Thermal Conductivity	22.0 W/m-K @Temperature <=20.0 °C	153 BTU-in/hr-ft²-°F @Temperature <=68.0 °F
CLAL-MSX ARCAP Anticorrosion AP1C H14 4/4 hard, Drawn Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un..
Thermal Conductivity	22.0 W/m-K @Temperature <=20.0 °C	153 BTU-in/hr-ft²-°F @Temperature <=68.0 °F
CLAL-MSX ARCAP Anticorrosion AP1 H11 1/4 hard, Drawn Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin..
Thermal Conductivity	22.0 W/m-K @Temperature <=20.0 °C	153 BTU-in/hr-ft²-°F @Temperature <=68.0 °F
CLAL-MSX ARCAP Anticorrosion AP1 H14 4/4 hard, Drawn Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin..
Thermal Conductivity	22.0 W/m-K @Temperature <=20.0 °C	153 BTU-in/hr-ft²-°F @Temperature <=68.0 °F
CLAL-MSX ARCAP Anticorrosion AP1C H12 1/2 hard, Drawn Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un..
Thermal Conductivity	22.0 W/m-K @Temperature <=20.0 °C	153 BTU-in/hr-ft²-°F @Temperature <=68.0 °F
CLAL-MSX ARCAP Anticorrosion AP1D H14 4/4 hard, Drawn Copper Alloy, Wire and rod, 5 High Corrosion Resistance: ARCAP alloys are very corrosion resistant to the majority of chemical and physical environments. CLAL can provide data for the corrosion resistance of ARCAP alloys. In par..
Thermal Conductivity	22.0 W/m-K @Temperature 20.0 °C	153 BTU-in/hr-ft²-°F @Temperature 68.0 °F	hardened and tempered
Bohler-Uddeholm UDDEHOLM VANADIS 30 AISI M2 + Co SUPERCLEAN 3 Powder Metallurgical Cold Work Tool Steel Uddeholm Vanadis 30 is a Co high alloyed powder metallurgy high speed steel corresponding to AISI M3:2 + Co. The high compressive strength, 67 HRC, and good abrasive wear resistance makes Uddeholm V..
Thermal Conductivity	22.0 W/m-K @Temperature 199 °C	153 BTU-in/hr-ft²-°F @Temperature 390 °F	hardness of 60 HRC
Bohler-Uddeholm UDDEHOLM VANADIS 6 Cold Work Tool Steel Description: Chromium-molybdenum-vanadium alloyed PM steel. Toolmaking with highly alloyed tool steel means that machining and heat treatment have to be considered more than with lower alloyed grade..
Thermal Conductivity	22.0 W/m-K @Temperature 704 °C	153 BTU-in/hr-ft²-°F @Temperature 1300 °F
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include ..