- Polymer Property : Thermal Conductivity = 194 BTU-in/hr-ft²-°F
Polymer Property : Thermal Conductivity = 194 BTU-in/hr-ft²-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 27.9 W/m-K @Temperature 100 °C |
194 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| QuesTek® Innovations Ferrium® M54™ Ultrahigh-strength Steel for Structural Applications Description: Ferrium® M54™ is an ultra high-strength steel for structural applications. Ferrium® M54™ was designed to provide mechanical properties equal to, or better than ultrahigh-strength st.. |
|||
| Thermal Conductivity | 27.9 W/m-K @Temperature 300 °C |
194 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| International Mold Steel Daido DRM2 Matrix High-Speed Steel This matrix type high speed tool steel is available for warm and cold forging tools where critical performance is required. DRM2 prolongs service life due to its higher hardness and toughness than t.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged 1300 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 27.9 W/m-K @Temperature 760 °C |
194 BTU-in/hr-ft²-°F @Temperature 1400 °F |
|
| Latrobe LSSâ„¢ H12 Hot Work Tool Steel (ASTM H12) TLS H12 hot work tool steel is a 5% chromium, general-purpose hot work steel that is characterized by excellent impact toughness. It contains less vanadium than the widely-used H13 hot work tool ste.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 400 °C |
194 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Assab Steels ASP 23 Cold Work Steel ASP 23 is a chromium-molybdenum-tungsten-vanadium alloyed high speed steel which is characterized by:High wear resistance (abrasive profile)High compressive strengthVery good through-hardening prope.. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||