Polymer Property : Thermal Conductivity = 79.1 BTU-in/hr-ftÂ²-Â°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Thermal Conductivity	11.4 W/m-K @Temperature 100 Â°C	79.1 BTU-in/hr-ftÂ²-Â°F @Temperature 212 Â°F
Haynes HastelloyÂ® C-4 alloy, all-weld metal, as welded, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900Â°F (649 to 1038Â°C) rang..
Thermal Conductivity	11.4 W/m-K @Temperature 100 Â°C	79.1 BTU-in/hr-ftÂ²-Â°F @Temperature 212 Â°F
Haynes HastelloyÂ® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours at 649Â°C (1200Â°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900Â°F (649 to 1038Â°C) rang..
Thermal Conductivity	11.4 W/m-K @Temperature 93.0 Â°C	79.1 BTU-in/hr-ftÂ²-Â°F @Temperature 199 Â°F	Annealed
Special Metals INCONELÂ® alloy 783 Ni-Co-Fe Alloy The newest of the high-performance superalloys invented by Special Metals Corporation, INCONELÂ® alloy 783 (UNS R30783/US Patent 5,478,417), is an oxidation-resistant, low expansion, nickel-cobalt..
Thermal Conductivity	11.4 W/m-K @Temperature 100 °C	79.1 BTU-in/hr-ft²-°F @Temperature 212 °F
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 10 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..
Thermal Conductivity	11.4 W/m-K @Temperature 100 °C	79.1 BTU-in/hr-ft²-°F @Temperature 212 °F
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..