- Polymer Property : Solidus = 1290 °C
Polymer Property : Solidus = 1290 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, 20% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, 40% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, plate after 16000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, plate after 4000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 10% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 30% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 5% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 50% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of .. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) + Aged 1400°F (760°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 2150°F (1180°C)/5 minutes/AC + Aged 1400°F (760°C)/100h/AC. This produces ASTM grain siz.. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Special Metals INCONEL® Alloy 625 Niobium content includes tantalum. A nickel-chromium-molybdenum alloy with an addition of niobium that acts with the molybdenum to stiffen the alloy's matrix and thereby provide high strength witho.. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Special Metals NIMONIC® Alloy 105 A precipitation-hardenable nickel-cobalt-chromium alloy with an addition of molybdenum for solid-solution strengthening. The relatively high aluminum content enhances both strength (through greater.. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Special Metals NIMONIC® Alloy 115 A precipitation-hardenable nickel-chromium-cobalt alloy with an addition of molybdenum for solid-solution strengthening. It is similar to NIMONIC alloy 105 but has higher levels of aluminum and tit.. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
| Solidus | 1290 °C | 2350 °F | |
| Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||