- Polymer Property : Specific Heat Capacity = 0.112 BTU/lb-°F
Polymer Property : Specific Heat Capacity = 0.112 BTU/lb-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2025°F (1107°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
| Specific Heat Capacity | 0.469 J/g-°C @Temperature 400 °C |
0.112 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Specific Heat Capacity | 0.469 J/g-°C @Temperature 400 °C |
0.112 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 316°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 427°C (800°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 649°C (1200°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 982°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes Ultimet® alloy, all-weld metal, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes Ultimet® alloy, all-weld metal, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes Ultimet® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes Ultimet® alloy, plate, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes Ultimet® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.468 J/g-°C @Temperature 400 °C |
0.112 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® alloy, flat products Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Specific Heat Capacity | 0.468 J/g-°C @Temperature 400 °C |
0.112 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Gas Tungsten Arc Welded (GTAW) All Weld Cruciform Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Specific Heat Capacity | 0.468 J/g-°C @Temperature 400 °C |
0.112 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Specific Heat Capacity | 0.468 J/g-°C @Temperature 400 °C |
0.112 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Specific Heat Capacity | 0.468 J/g-°C @Temperature 400 °C |
0.112 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
| Specific Heat Capacity | 0.470 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Sheet, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||
| Specific Heat Capacity | 0.469 J/g-°C @Temperature 400 °C |
0.112 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Specific Heat Capacity | 0.469 J/g-°C @Temperature 400 °C |
0.112 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Specific Heat Capacity | 0.468 J/g-°C @Temperature 400 °C |
0.112 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C) Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Specific Heat Capacity | 0.469 J/g-°C @Temperature 400 °C |
0.112 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Specific Heat Capacity | 0.468 J/g-°C @Temperature 100 °C |
0.112 BTU/lb-°F @Temperature 212 °F |
|
| Special Metals NIMONIC® alloy 91 Ni-Cr-Co Alloy NIMONIC® alloy 91 is a wrought nickel-chromium-cobalt based alloy strengthened by additions of aluminum and titanium.This alloy is a modification of NIMONIC alloy 90, but has an increased chromium .. |
|||