Polymer Property : Drying Temperature = 89.0 °C Product List

Processing Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Processing Properties	Metric	English	Comments
Drying Temperature	89.0 - 90.0 °C	192 - 194 °F	Drying generally not required. If it is required, drying at 80-90°C for 3-4 hours will suffice.
Asahi Kasei Tenac® 2013A Acetal Homopolymer, UV Stabilized (discontinued **) Similar to 3013A, but higher in molecular weight.Applications: Pipe fittings, rollers, exterior automotive parts.This product is not a part of the standard product line dated 2003.
Drying Temperature	89.0 - 90.0 °C	192 - 194 °F	Drying generally not required. If it is required, drying at 80-90°C for 3-4 hours will suffice.
Asahi Kasei Tenac® 5012 Acetal Homopolymer (discontinued **) Standard-flow grade, with reduced stiffness and increased elongation through addition of special polymers.Applications: Clips, fasteners, press-fit parts.This product is not a part of the standard p..
Drying Temperature	89.0 - 90.0 °C	192 - 194 °F	Drying generally not required. If it is required, drying at 80-90°C for 3-4 hours will suffice.
Asahi Kasei Tenac® GT525 Acetal Homopolymer, 25% Glass Beads (discontinued **) 25% glass beads-filled grade with superior isotropic dimensional stability.Applications: Speedometer frames.This product is not a part of the standard product line dated 2003.
Drying Temperature	89.0 - 90.0 °C	192 - 194 °F	Drying generally not required. If it is required, drying at 80-90°C for 3-4 hours will suffice.
Asahi Kasei Tenac® LT805 Acetal Homopolymer, Low Friction Grade (discontinued **) Excellent friction and wear on metals.Applications: Keyboard parts, bearings for office machines, gears.This product is not a part of the standard product line dated 2003.
Drying Temperature	89.0 - 90.0 °C	192 - 194 °F	Drying generally not required. If it is required, drying at 80-90°C for 3-4 hours will suffice.
Asahi Kasei Tenac® FA405 Acetal Homopolymer, Low Friction Grade (discontinued **) Contains fluoropolymer and lubricant; excellent friction and wear on plastics.Applications: Bearings for printers, cams, gears.This product is not a part of the standard product line dated 2003.
Drying Temperature	89.0 - 90.0 °C	192 - 194 °F	Drying generally not required. If it is required, drying at 80-90°C for 3-4 hours will suffice.
Asahi Kasei Tenac® LA531 Acetal Homopolymer, High Lubricity (discontinued **) High-lubricity block copolymer with excellent friction and wear characteristics, especially on POM.Applications: Gears, keyboard parts.This product is not a part of the standard product line dated 2..