Polymer Property : Annealing Temperature = 1010 °C Product List

Processing Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Processing Properties	Metric	English	Comments
Annealing Temperature	1010 - 1040 °C	1850 - 1900 °F	Stress Relief Annealing (min. 0.5 h)
Outokumpu 353MA® High Temperature Austenitic Stainless Steel Alloy with higher nickel content than the other steels. Has increased silicon and nitrogen contents and is microalloyed with rare earth metals (REM). Max service temperature in air is 1150°C, but..
Annealing Temperature	1010 - 1040 °C	1850 - 1900 °F	Stress Relief Annealing (min. 0.5 h)
Outokumpu 4828 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and ..
Annealing Temperature	1010 - 1040 °C	1850 - 1900 °F	Stress Relief Annealing (min. 0.5 h)
Outokumpu 4833 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and ..
Annealing Temperature	1010 - 1090 Â°C	1850 - 2000 Â°F	Followed by rapid cooling with forced air or water quenching
Schmolz + Bickenbach UGIMAÂ® 303 HD Stainless Steel Bar Description: 303 UGIMA HDâ„¢ is a low sulfur version of Ugitechâ€™s improved machining 303 grade. It is designed to provide better metallurgical performance with respect to weldability, corros..
Annealing Temperature	1010 - 1090 Â°C	1850 - 2000 Â°F	Followed by rapid cooling with forced air or water quenching
Schmolz + Bickenbach UGIMAÂ® 303 Stainless Steel Bar Description: 303 UGIMAÂ® is Ugitechâ€™s improved machining grade produced only by Ugitech. It is identical in every way to regular 303, except with respect to machinability. 303 UGIMAÂ® repre..
Annealing Temperature	1010 - 1090 Â°C	1850 - 2000 Â°F	followed by rapid cooling with forced air or water quenching
Schmolz + Bickenbach UGIMAÂ® 316/316L Stainless Steel Bar Description: 316/316L UGIMAÂ® is Ugitechâ€™s improved machining grade produced only by Ugitech. It is identical in every way to regular 316L, except with respect to machinability. 316/316L UGIM..
Annealing Temperature	1010 - 1090 °C	1850 - 2000 °F	followed by rapid cooling with forced air or water quenching
Schmolz + Bickenbach UGIMA 304/304L® Stainless Steel Bar Description: 304/304L UGIMA® is the next generation of improved high machinability grades from Ugitech. The UGIMA® grades have redefined high machinability stainless steels, showing improvements o..