Processing Properties | Metric | English | Comments |
---|---|---|---|
Annealing Temperature | 800 - 850 °C | 1470 - 1560 °F | Cooling: forced air or water |
Outokumpu 4724 High Temperature Ferritic Stainless Steel Truly stainless high temperature grade with 13% chromium. Not critical in terms of embrittlement.Applications: Mostly used in high temperature applications with sulphurous atmospheres and/or low te.. |
|||
Annealing Temperature | 800 - 850 °C | 1470 - 1560 °F | Cooling: forced air or water |
Outokumpu 4742 High Temperature Ferritic Stainless Steel Good scaling resistance and can be subjected to reducing sulphur environments without risk. Subject to 475°C embrittlement and grain coarsening at temperatures above 950°C. s-phase may form afte.. |
|||
Annealing Temperature | 800 - 850 °C | 1470 - 1560 °F | Cooling: forced air or water |
Outokumpu 4762 High Temperature Ferritic Stainless Steel Highest chromium content-most resistant to reducing sulphurous gases. Susceptible to 475°C embrittlement and s-phase forms during long exposures in the range 600-800°C.Applications: Mostly used i.. |
|||
Annealing Temperature | 801.7 - 849 °C | 1475 - 1560 °F | Soft; Cooling: Furnace 20°F/hour to 1200°F/ Then air cool; < 231 HB |
Schmolz + Bickenbach Cryodur® 2363 (A-2) Cold Work Die Steel Description: Cryodur® 2363 is a cold-work steel developed for an excellent combination of wear resistance and toughness and Supplied in the annealed conditionCharacteristics: Good wear resistance; .. |