- Polymer Property : Electrical Resistivity = 0.000132 ohm-cm
Polymer Property : Electrical Resistivity = 0.000132 ohm-cm Product List
Electrical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 400 °C |
0.000132 ohm-cm @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Gas Tungsten Arc Welded (GTAW) All Weld Cruciform Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 400 °C |
0.000132 ohm-cm @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 400 °C |
0.000132 ohm-cm @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Shielded Metal Arc Welded (SMAW) All Weld Cruciform Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 400 °C |
0.000132 ohm-cm @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 400 °C |
0.000132 ohm-cm @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 400 °C |
0.000132 ohm-cm @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 600 °C |
0.000132 ohm-cm @Temperature 1110 °F |
|
| Haynes Hastelloy® C-4 alloy, all-weld metal, as welded, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 600 °C |
0.000132 ohm-cm @Temperature 1110 °F |
|
| Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 600 °C |
0.000132 ohm-cm @Temperature 1110 °F |
|
| Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 600 °C |
0.000132 ohm-cm @Temperature 1110 °F |
|
| Haynes Hastelloy® C-4 alloy, sheet, aged 100 hours at 899°C Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 600 °C |
0.000132 ohm-cm @Temperature 1110 °F |
|
| Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 10 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 600 °C |
0.000132 ohm-cm @Temperature 1110 °F |
|
| Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
| Electrical Resistivity | 0.000132 ohm-cm @Temperature 400 °C |
0.000132 ohm-cm @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C) Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||