Polymer Property : Hot Wire Ignition, HWI = 2.0 sec Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Electrical Properties	Metric	English	Comments
Hot Wire Ignition, HWI	2.0 sec @Thickness >=1.50 mm	2.0 sec @Thickness >=0.0591 in	ASTM D3874-88
BASF Ultramid® B3UG4 Grey 22975 20% Glass Filled PA66 FR (Conditioned) Description: Halogen-free and phosphorus free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire..
Hot Wire Ignition, HWI	2.0 sec @Thickness >=1.50 mm	2.0 sec @Thickness >=0.0591 in	ASTM D3874-88
BASF Ultramid® B3UG4 Grey 22975 20% Glass Filled PA66 FR (Dry) Description: Halogen-free and phosphorus free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire..
Hot Wire Ignition, HWI	2.0 sec @Thickness >=1.50 mm	2.0 sec @Thickness >=0.0591 in	ASTM D3874-88
BASF Ultramid® B3UG4 LS BK 23215 20% Glass Filled PA66 FR (Conditioned) Description: Halogen-free and phosphorus free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire..
Hot Wire Ignition, HWI	2.0 sec @Thickness >=1.50 mm	2.0 sec @Thickness >=0.0591 in	ASTM D3874-88
BASF Ultramid® B3UG4 LS BK 23215 20% Glass Filled PA66 FR (Dry) Description: Halogen-free and phosphorus free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire..
Hot Wire Ignition, HWI	2.0 sec @Thickness >=1.50 mm	2.0 sec @Thickness >=0.0591 in	ASTM D3874-88
BASF Ultramid® B3UG4 LS Grey 22985 20% Glass Filled PA66 FR (Conditioned) Description: Halogen-free and phosphorus free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire..
Hot Wire Ignition, HWI	2.0 sec @Thickness >=1.50 mm	2.0 sec @Thickness >=0.0591 in	ASTM D3874-88
BASF Ultramid® B3UG4 LS Grey22985 20% Glass Filled PA66 FR (Dry) Description: Halogen-free and phosphorus free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire..