- ATI Allvac® Nickelvac® 901 Nickel Superalloy, Heat Treatment: 1010°C (1850°F) + Age
ATI Allvac® Nickelvac® 901 Nickel Superalloy, Heat Treatment: 1010°C (1850°F) + Age
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | ATI Allvac |
| Trade Name | Nickelvac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ATI Allvac® Nickelvac® 901 Nickel Superalloy, Heat Treatment: 1010°C (1850°F) + Age.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Allvac.Applications: Turbine discs and shafts, compressor blades and discs, high-temperature bolting, high-temperature devices, cryogenics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.22 g/cc | 0.297 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C value for Brinell test with 3000 kg load/10 mm diameter ball |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C value. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C value. |
| Tensile Strength, Ultimate | 1276 MPa | 185100 psi | |
| Tensile Strength, Yield | 1172 MPa @Strain 0.200 % |
170000 psi @Strain 0.200 % |
|
| Elongation at Break | 25 % | 25 % | |
| Reduction of Area | 40 % | 40 % |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Boron, B | 0.015 % | 0.015 % | |
| Carbon, C | 0.050 % | 0.050 % | |
| Chromium, Cr | 12.5 % | 12.5 % | |
| Iron, Fe | 36 % | 36 % | as balance |
| Molybdenum, Mo | 6.0 % | 6.0 % | |
| Nickel, Ni | 43 % | 43 % | |
| Titanium, Ti | 2.8 % | 2.8 % |