BASF Capron® 8233G 33% Glass-Filled Nylon 6 (Conditioned)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® 8233G 33% Glass-Filled Nylon 6 (Conditioned)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Capron 8233G is a 33% glass fiber reinforced polyamide 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also available in heat stabilized (Capron 8233G HS) and/or pigmented versions.Capron 8233G is generally recommended for applications such as power tool housings, weed trimmer components, gears, automotive housings and under hood applications.Data provided by Allied Signal.Processing: Max. water content 0.12%. Product is supplied in sealed containers and drying is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 85°C (185 °F). Is recommended. Drying time is dependent on moisture level.Melt Temperature: 270-295 degC (518-563 degF). Mold Temperature: 80-95 degC (176-203 degF). Injection and Packing Pressure: 35-125 bar (500-1500psi) This product can be processed over a wide range of mold temperatures; however, for applications where aesthetics critical, a mold surface temperature of 80-95 degC (176-203 degF) is required. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Back pressure can be utilized to provide uniform melt consistency and reduce trapped air and gas. A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate. Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
(Dry)
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM Data MD (Dry)
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
ISO Data (Dry)
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 125 MPa
18100 psi
ASTM data at 5 mm/min.
Tensile Strength, Yield 115 MPa
16700 psi
50 mm/min; Same value from ASTM and ISO test.
Elongation at Break 6.0 %
6.0 %
Nominal
6.0 %
6.0 %
ASTM, 5 mm/minl
Elongation at Yield 5.9 %
5.9 %
ISO Value at 50 mm/min.
6.0 %
6.0 %
ASTM Value at 50 mm/min.
Tensile Modulus 5.84 GPa
847 ksi
same value from ASTM and ISO test.
Flexural Yield Strength 180 MPa
26100 psi
ASTM Data
Flexural Modulus 5.125 GPa
743.3 ksi
ASTM Data
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
(Dry)
Processing Properties Metric English Comments
Drying Temperature 85.0 °C
185 °F
See Materials Notes