BASF Ultramid® 82335G HS BK 102 50% Glass Filled PA6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 82335G HS BK 102 50% Glass Filled PA6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Ultramid 8235G HS BK-102 is a heat stabilized, pigmented black, 50% glass fiber reinforced PA6 injection molding compound offering excellent level of strength, stiffness, high temperature performance and dimensional stability. Its resistance to creep under load is excellent. It is available in natural, black, weather resistance and pigmented versions.Applications: Ultramid 8235G HS BK-102 is generally recommended for applications such as power tool housings, cattle ear taggers, luggage frames, fans and pressure regulator housings.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.4 % | 1.4 % | 50% RH; ISO 62 |
| 4.8 % | 4.8 % | Saturation; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 210 MPa | 30500 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Tensile Modulus | 1.58 GPa | 229 ksi | ISO 527 |
| Flexural Strength | 300 MPa | 43500 psi | ISO 178 |
| Flexural Modulus | 13.2 GPa | 1910 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature -40.0 °C |
5.71 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 305 °C | 536 - 581 °F | |
| Mold Temperature | 80.0 - 95.0 °C | 176 - 203 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | >= 0.060 % | >= 0.060 % | |
| Injection Pressure | 35.0 - 125 MPa | 5080 - 18100 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK 102 | |
| Commercial Status | North America |