BASF Ultramid® B50L 01 PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B50L 01 PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid B50L 01 is a high-viscosity, lubricated, general-purpose extrusion PA6 grade. It conforms to FDA requirements including, 21 CFR 177.1500,EU Directive 2002/72/EC, the German BfR recommendation "X Polyamide", 1.6.1998 or legislations for other countries will be provided on request.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
dry; ISO 1183
Water Absorption 9.5 %
9.5 %
beginning dry; ISO 62
Moisture Absorption at Equilibrium 2.6 %
2.6 %
beginning dry (23°C/50% R.H.); ISO 62
Relative Viscosity 5.0 cP
5.0 cP
ISO Test; 96 % SAV
Viscosity Test 320 cm³/g
320 cm³/g
Viscosity number
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
ASTM Data; MD
Melt Flow 8.0 g/10 min

@Load 5.00 kg,
Temperature 275 °C
8.0 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 45.0 MPa
6530 psi
50mm/min; ISO 527
Elongation at Break >= 50 %
>= 50 %
50mm/min, Nominal strain; ISO 527
Elongation at Yield 20 %
20 %
50mm/min; ISO 527
Tensile Modulus 1.00 GPa
145 ksi
1mm/min; ISO 527
Tensile Creep Modulus, 1 hour 950 MPa
138000 psi
ISO 899
Tensile Creep Modulus, 1000 hours 850 MPa
123000 psi
ISO 899
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Descriptive Properties Value Comments
Color Natural
Commercial Status North America and Europe
FDA 21 CFR 177.1500
Form Pellets
Impact Modified No
Primary Processing Technique Film Extrusion
Processing Film Extrusion
Profile Extrusion