Carpenter Pyromet® CTX-3 Superalloy, Heat Treated

Category Metal , Superalloy , Iron Base
Manufacturer Carpenter Technology Corporation (Cartech)
Trade Name Pyromet®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Carpenter Pyromet® CTX-3 Superalloy, Heat Treated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by Carpenter Technology Corporation.Pyromet® alloy CTX-3 is a high strength, precipitation hardenable superalloy which exhibits a low CTE over a broad temperature range. This alloy also possess high hot hardness and good thermal fatigue resistance. It is weldable, brazable, and can be chromium plated. This material offers significant improvement in notched stress-rupture strength over Pyromet alloy CTX-1. Retained hot-cold work is not required for good stress rupture properties and is not affected by stress orientation.Pyromet® is a registered trademark of Carpenter Technology Corporation.
Physical Properties Metric English Comments
Density 8.28 g/cc
0.299 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1180 MPa
171000 psi
1040 MPa

@Temperature 538 °C
151000 psi

@Temperature 1000 °F
Tensile Strength, Yield 830 MPa

@Strain 0.200 %
120000 psi

@Strain 0.200 %
673 MPa

@Strain 0.200 %,
Temperature 538 °C
97600 psi

@Strain 0.200 %,
Temperature 1000 °F
Elongation at Break 14 %
14 %
In 50 mm
16 %

@Temperature 538 °C
16 %

@Temperature 1000 °F
In 50 mm
Reduction of Area 23 %
23 %
39 %

@Temperature 538 °C
39 %

@Temperature 1000 °F
Modulus of Elasticity 159.9 GPa
23190 ksi
Thermal Properties Metric English Comments
CTE, linear 7.50 µm/m-°C

@Temperature 25.0 - 416 °C
4.17 µin/in-°F

@Temperature 77.0 - 781 °F
7.70 µm/m-°C

@Temperature 25.0 - 260 °C
4.28 µin/in-°F

@Temperature 77.0 - 500 °F
Component Elements Properties Metric English Comments
Aluminum, Al <= 0.25 %
<= 0.25 %
Boron, B <= 0.012 %
<= 0.012 %
Carbon, C <= 0.050 %
<= 0.050 %
Chromium, Cr <= 0.50 %
<= 0.50 %
Cobalt, Co 13 - 15 %
13 - 15 %
Copper, Cu <= 0.50 %
<= 0.50 %
Iron, Fe 39 %
39 %
as remainder
Manganese, Mn <= 0.50 %
<= 0.50 %
Nb + Ta 4.5 - 5.5 %
4.5 - 5.5 %
Nickel, Ni 37 - 39 %
37 - 39 %
Niobium, Nb (Columbium, Cb) <= 5.5 %
<= 5.5 %
Phosphorous, P <= 0.015 %
<= 0.015 %
Silicon, Si <= 0.50 %
<= 0.50 %
Sulfur, S <= 0.015 %
<= 0.015 %
Tantalum, Ta <= 5.5 %
<= 5.5 %
Titanium, Ti 1.25 - 1.75 %
1.25 - 1.75 %