DuPont Teijin Films Teonex® Q83 Polyester Film, 200 Gauge

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer DuPont Teijin Films (DTF)
Trade Name Teonex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Teijin Films Teonex® Q83 Polyester Film, 200 Gauge.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Teonex® Q83 is biaxially oriented, slightly hazy polyethylene naphthalate (PEN) film with excellent handling properties and high dimensional stability. It is commercially available in 100, 200 and 300 gauge (25, 50, 75 micron).Approvals: UL 94 VTM-2 - for 100 through 300 gauge (0.025 - 0.075 mm) and UL Component Registration (RTI = 180/160°C) - Relative Thermal Index (RTI) = 180°C (Elect), 160°C (Mech)Also available in 100 and 300 GaugeInformation provided by DuPont.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
JIS C-2151
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 118 %
118 %
JIS C-2318 (Modified to TDF)
Film Elongation at Break, TD 115 %
115 %
JIS C-2318 (Modified to TDF)
Secant Modulus, MD 6.35 GPa
921 ksi
ASTM D822 (Modified to TDF)
Secant Modulus, TD 7.019 GPa
1018 ksi
ASTM D822 (Modified to TDF)
Coefficient of Friction, Dynamic 0.30
0.30
ASTM D1894
Coefficient of Friction, Static 0.30
0.30
ASTM D1894
Film Tensile Strength at Break, MD 207 MPa
30000 psi
JIS C-2318 (Modified to TDF)
Film Tensile Strength at Break, TD 234 MPa
34000 psi
JIS C-2318 (Modified to TDF)
Thermal Properties Metric English Comments
Melting Point 269 °C
516 °F
DSC
Glass Transition Temp, Tg 121 °C
250 °F
DSC
UL RTI, Electrical 160 °C
320 °F
UL RTI, Mechanical without Impact 180 °C
356 °F
Shrinkage, MD 0.090 %

@Temperature 150 °C
0.090 %

@Temperature 302 °F
JIS C-2318 (Modified to TDF)
0.30 %

@Temperature 200 °C,
Time 600 sec
0.30 %

@Temperature 392 °F,
Time 0.167 hour
Unrestrained
Shrinkage, TD 0.00 %

@Temperature 150 °C
0.00 %

@Temperature 302 °F
JIS C-2318 (Modified to TDF)
0.050 %

@Temperature 200 °C,
Time 600 sec
0.050 %

@Temperature 392 °F,
Time 0.167 hour
Unrestrained
Optical Properties Metric English Comments
Haze 12 %
12 %
JIS K6714
Transmission, Visible 84 %
84 %
JIS K6714
UV Transmittance 11 %

@Wavelength 360 nm
11 %

@Wavelength 360 nm
TDF Method
Electrical Properties Metric English Comments
Volume Resistivity 2.90e+17 ohm-cm
2.90e+17 ohm-cm
JIS C-2318
Dielectric Constant 2.8

@Frequency 100000 Hz
2.8

@Frequency 100000 Hz
JIS C-2318
2.9

@Frequency 60.0 Hz
2.9

@Frequency 60.0 Hz
JIS C-2318
Descriptive Properties Value Comments
F5 21 kpsi
TD, TDF Method
21 kpsi
MD, TDF Method
Surface Roughness 13 nm
TDF Method (Inside)
Tear Propagation 2.0 lb
MD, TDF Method
2.0 lb
TD, TDF Method