E-Polymers SEPAZ® N3040HI Nanoclay 4% High Impact Nano Composite Resin

Category Polymer , Thermoplastic
Manufacturer E-Polymers Co. Ltd.
Trade Name SEPAZ®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF E-Polymers SEPAZ® N3040HI Nanoclay 4% High Impact Nano Composite Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nanocomposite: SEPAZ Nano PA6 nanocomposites have been prepared successfully in commercial scale through 'in situ' polymerization or melt extrusion. The unique performance properties of nanocomposities provide a great flexibility in materials design. Nanocomposites have been formulated into various resin systems to deliver desired properties: from rheology control to fire retardation. It shows low specific gravity, gas permeability and high heat resistance, rigidity, dimension stability used for underhood and fuel line parts in automotive industry and for packaging film in food industry.Information Provided by E-Polymers Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
ASTM D792
Water Absorption 0.70 %

@Time 86400 sec
0.70 %

@Time 24.0 hour
Linear Mold Shrinkage 0.0080 cm/cm
0.0080 in/in
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
Mechanical Properties Metric English Comments
Tensile Strength 68.67 MPa
9960 psi
ASTM D638
Elongation at Break 15 %
15 %
ASTM D638
Flexural Strength 98.1 MPa
14200 psi
ASTM D790
Flexural Modulus 2.4525 GPa
355.71 ksi
ASTM D790
Izod Impact, Notched 1.27 J/cm
2.39 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 100 °C
212 °F
ASTM D648
Flammability, UL94 HB
HB
Processing Properties Metric English Comments
Melt Temperature 224 °C
435 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F