EDRO RoyAlloy™ #6 Free Machining Stainless Holder Steel

Category Metal , Ferrous Metal , Martensitic , Stainless Steel , T 400 Series Stainless Steel
Manufacturer EDRO
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF EDRO RoyAlloy™ #6 Free Machining Stainless Holder Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
RoyAlloy™ is a 400 series martensitic stainless steel supplied prehardened. RoyAlloy™ is characterized by excellent machinability, good corrosion resistance, uniform and consistent hardness in all dimensions, good resistance to indentation (compressive strength), excellent ductility, excellent flatness, dimensionally stable, smooth as rolled surfaces, excellent weldability, and good thermal conductivity. RoyAlloy™ is an improved stainless grade designed specifically for plastic molding applications. Chemical composition and thermal treatments provide physical properties and microstructures designed to provide reduced mold maintenance costs, worry free weld repair, dimensional stability, and lower mold production costs due to less cutting tool wear and increased cutting speeds. Applications: plastic and rubber molds, plastic mold bases, plastic mold inserts, constructional parts, plastic extrusionInformation provided by EDRO
Physical Properties Metric English Comments
Density 7.81 g/cc

@Temperature 199 °C
0.282 lb/in³

@Temperature 390 °F
Prehardened to 321 HB
7.86 g/cc

@Temperature 20.0 °C
0.284 lb/in³

@Temperature 68.0 °F
Prehardened to 321 HB
Mechanical Properties Metric English Comments
Hardness, Brinell 321
321
Tensile Strength, Ultimate 1050 MPa

@Temperature 199 °C
152000 psi

@Temperature 390 °F
Longitudinal Tests from 3" rolled plate at 321 HB
1070 MPa

@Temperature 20.0 °C
155000 psi

@Temperature 68.0 °F
Longitudinal Tests from 3" rolled plate at 321 HB
Tensile Strength, Yield 869 MPa

@Strain 0.200 %,
Temperature 199 °C
126000 psi

@Strain 0.200 %,
Temperature 390 °F
Longitudinal Tests from 3" rolled plate at 321 HB
889 MPa

@Strain 0.200 %,
Temperature 20.0 °C
129000 psi

@Strain 0.200 %,
Temperature 68.0 °F
Longitudinal Tests from 3" rolled plate at 321 HB
Elongation at Yield 12 %

@Temperature 20.0 °C
12 %

@Temperature 68.0 °F
in 2"
12 %

@Temperature 199 °C
12 %

@Temperature 390 °F
in 2"
Reduction of Area 34 %

@Temperature 20.0 °C
34 %

@Temperature 68.0 °F
34 %

@Temperature 199 °C
34 %

@Temperature 390 °F
Modulus of Elasticity 190 GPa

@Temperature 199 °C
27600 ksi

@Temperature 390 °F
200 GPa

@Temperature 20.0 °C
29000 ksi

@Temperature 68.0 °F
Charpy Impact 21.7 J

@Temperature 20.0 °C
16.0 ft-lb

@Temperature 68.0 °F
Longitudinal Charpy V-notch Tests from a 3" rolled plate at 321 HB
35.3 J

@Temperature 199 °C
26.0 ft-lb

@Temperature 390 °F
Longitudinal Charpy V-notch Tests from a 3" rolled plate at 321 HB
Thermal Properties Metric English Comments
CTE, linear 11.0 µm/m-°C

@Temperature 20.0 - 199 °C
6.10 µin/in-°F

@Temperature 68.0 - 390 °F
Descriptive Properties Value Comments
Color Code Yellow Blue Stripe