ExxonMobil Label-Lyte™ 60ZH247 OPP Film

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Label-Lyte™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Label-Lyte™ 60ZH247 OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A super white opaque, caviated BOPP film for Pressure Sensitive (PSA) labeling applications where good optical properties are required. 60ZH247 also shows excellent performances on reel-fed wrap-around labeling machines, where its high stiffness is particularly appreciated.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Outstanding white opaque background and superb white gloss finishGood printability on outside tread sideCompatibility with most flex resistanceVery good moisture resistanceGood overall converting, diecutting, and dispensing propertiesApplications: BakeryBeverage, AlcoholicBeverage, Carbonated Beverage, Mineral WatersBiscuits/Cookie/Crackers Dairy Products Dry Foods and Beverage PowdersHealth and Beauty CareHousehold and DetergentsIndustrial Uses: Pressure Sensitive LabelsProcessing Method: Inner Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported, UV Flexographic Printing, UV Letterpress Printing, UV Offset Lithography Printing and Water-based Flexographic PrintingInformation provided by ExxonMobil
Physical Properties Metric English Comments
Thickness 61.0 microns
2.40 mil
ExxonMobil Method
Coating Weight 42.9 g/m²
26.8 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 170 %
170 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD 55 %
55 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, MD 105 MPa
15200 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 185 MPa
26800 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 5.0 %

@Temperature 135 °C,
Time 432 sec
5.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Shrinkage, TD 3.0 %

@Temperature 135 °C,
Time 432 sec
3.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Optical Properties Metric English Comments
Gloss 70 %
70 %
45°; ExxonMobil Method
Transmission, Visible 20 %
20 %
ExxonMobil Method
Descriptive Properties Value Comments
Yield 16100 in2/lb