Honeywell Capran® Unidraw (0.75 mil) Nylon 6 Film  (discontinued **)

Category Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Honeywell Capran® Unidraw (0.75 mil) Nylon 6 Film  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Capran® Unidraw is a 0.75 mil (19 micron) machine direction oriented nylon 6 film specifically designed for the continuous process lamination of glass fiber reinforced panel. High strength in the machine direction allows for faster, more reliable production with fewer machine tears. It releases well from cured panels whether they are hot, cold, wet, or dry. Information provided by Honeywell.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0410 lb/in³
Yield Density
Thickness 19.0 microns
0.750 mil
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 60 - 80 %
60 - 80 %
ASTM D882
Film Elongation at Break, TD 400 - 450 %
400 - 450 %
ASTM D882
Secant Modulus, MD 2.069 - 2.93 GPa
300.1 - 425 ksi
ASTM D882
Secant Modulus, TD 2.069 - 2.93 GPa
300.1 - 425 ksi
ASTM D882
Coefficient of Friction 0.20 - 0.60
0.20 - 0.60
film to stainless steel; ASTM D1894
0.70 - 1.2
0.70 - 1.2
film to film; ASTM D1894
Tear Strength Test 1200 - 1500
1200 - 1500
graves tear MD, grams/mil; ASTM D1004
1200 - 1600
1200 - 1600
graves tear TD, grams/mil; ASTM D1004
Elmendorf Tear Strength, MD 1.57 - 4.21 g/micron
40.0 - 107 g/mil
Elmendorf Tear Strength, TD 5.25 - 7.87 g/micron
133 - 200 g/mil
ASTM D1922
Film Tensile Strength at Break, MD 310 - 379 MPa
45000 - 55000 psi
ASTM D882
Film Tensile Strength at Break, TD 93.1 - 114 MPa
13500 - 16500 psi
ASTM D882
Thermal Properties Metric English Comments
Shrinkage, MD 8.0 - 15 %
8.0 - 15 %
400°F / 201°C - 5 min.; ASTM D1204
Shrinkage, TD 1.0 - 2.5 %
1.0 - 2.5 %
400°F / 201°C - 5 min.; ASTM D1204
Optical Properties Metric English Comments
Haze <= 5.0 %
<= 5.0 %
ASTM D1003
Gloss 80 - 100 %
80 - 100 %
at 45°