LATI Latistat 62-06 K/10 PA6, 10% Carbon Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Carbon Fiber Filled
Manufacturer LATI
Trade Name Latistat
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latistat 62-06 K/10 PA6, 10% Carbon Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Dissipative product based on Polyamide 6 (PA6). Carbon fiber. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
Linear Mold Shrinkage, Flow 0.0040 - 0.0055 cm/cm
0.0040 - 0.0055 in/in
Linear Mold Shrinkage, Transverse 0.0105 - 0.0135 cm/cm
0.0105 - 0.0135 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 115 MPa
16700 psi
Elongation at Break 6.5 %
6.5 %
Elongation at Yield 3.5 %
3.5 %
Tensile Modulus 8.10 GPa
1170 ksi
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
Vicat Softening Point 205 °C

@Load 5.00 kg
401 °F

@Load 11.0 lb
Electrical Properties Metric English Comments
Surface Resistance 5000 ohm
5000 ohm
Processing Properties Metric English Comments
Melt Temperature 240 - 280 °C
464 - 536 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa