Ravago Manufacturing Americas Hybrid S555 ABS + Polycarbonate Alloy

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Ravago Manufacturing Americas, LLC
Trade Name Hybrid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ravago Manufacturing Americas Hybrid S555 ABS + Polycarbonate Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ravago.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ISO 294-4
0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 21 g/10 min
21 g/10 min
ASTM D1238
28.32 g/10 min
28.32 g/10 min
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 62.0 MPa
8990 psi
ISO 527-1,-2
63.4 MPa
9200 psi
ASTM D638
Elongation at Break 45 %
45 %
ASTM D638
48 %
48 %
ISO 527-1,-2
Flexural Strength 83.0 MPa
12000 psi
ISO 178
Flexural Yield Strength 84.1 MPa
12200 psi
ASTM D790
Flexural Modulus 2.55 GPa
370 ksi
ISO 178
2.55 GPa
370 ksi
ASTM D790
Izod Impact, Notched 6.41 J/cm
12.0 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 44.0 kJ/m²
20.9 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 105 °C
221 °F
ISO 75A-1,-2
107 °C
224 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 90.6 °C
195 °F
ISO 75A-1,-2
93.9 °C
201 °F
ASTM D648
Vicat Softening Point 110 °C
230 °F
ASTM D1525
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Internal Test
5VB

@Thickness 2.50 mm
5VB

@Thickness 0.0984 in
Internal Test
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
Internal Test