Reliance Industries Reclair O21010 Polyethylene

Category	Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded
Manufacturer	Reliance Industries
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Reliance Industries Reclair O21010 Polyethylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Octene comonomer based Linear Low Density Polyethylene. Blow film grade. Contains an optimum level of antioxidants and polymer processing aids. Designed for lamination film applications. Characteristics: good optical properties, good adhesion to substrate.Information provided by Reliance Industries

Physical Properties	Metric	English	Comments
Density	0.918 g/cc	0.0332 lb/in³	ASTM D1505
Melt Flow	0.90 g/10 min @Load 2.16 kg	0.90 g/10 min @Load 4.76 lb	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	12.5 MPa	1810 psi	ASTM D882
Film Tensile Strength at Yield, TD	13.0 MPa	1890 psi	ASTM D882
Film Elongation at Break, MD	750 %	750 %	ASTM D882
Film Elongation at Break, TD	950 %	950 %	ASTM D882
Coefficient of Friction, Dynamic	0.50	0.50	ASTM D1894
Coefficient of Friction, Static	0.58	0.58	ASTM D1894
Elmendorf Tear Strength, MD	13.8 g/micron	351 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	27.6 g/micron	701 g/mil	ASTM D1922
Dart Drop	7.00 g/micron	178 g/mil	F<sub>50</sub>,38mm dart 66mm height; ASTM D1709
Film Tensile Strength at Break, MD	45.0 MPa	6530 psi	ASTM D882
Film Tensile Strength at Break, TD	40.0 MPa	5800 psi	ASTM D882

Optical Properties	Metric	English	Comments
Gloss	80 %	80 %	60; ASTM D523