SABIC Innovative Plastics LNP LUBRICOMP RL003 PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP RL003 PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* RL003 is a compound based on Nylon 66 resin containing 15% PTFE. Added features of this material include: Wear Resistant.
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow >= 0.020 cm/cm

@Time 86400 sec
 >= 0.020 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
 0.010 - 0.030 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 73.0 MPa
10600 psi
ASTM D638
73.0 MPa
10600 psi
ISO 527
Elongation at Break 8.9 %
8.9 %
ISO 527
11 %
11 %
ASTM D638
Flexural Strength 90.0 MPa
13100 psi
ISO 178
103 MPa
14900 psi
ASTM D790
Flexural Modulus 2.90 GPa
421 ksi
ISO 178
Izod Impact, Notched 0.320 J/cm
0.599 ft-lb/in
ASTM D256
Izod Impact, Unnotched 10.14 J/cm
19.00 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Coefficient of Friction, Dynamic 0.32
0.32
ASTM D3702 Modified
Coefficient of Friction, Static 0.30
0.30
ASTM D3702 Modified
K (wear) Factor 56.4 x 10-8 mm³/N-M
28.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 82.0 °C
180 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af