SABIC Innovative Plastics LNP STAT-KON DX13320C PC COPOLYMER (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON DX13320C PC COPOLYMER (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Statkon DX13320C is ultra clean polycarbonate/carbon fiber compound with high modulus, good flow ability, easy mold release, and high level of cleanliness for the most demanding application. A unique feature of this material is its low C18-C40 hydrocarbons. This compound is manufactured using LNP CCS Technology.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.00050 - 0.0015 cm/cm

@Time 86400 sec
0.00050 - 0.0015 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ASTM D955
Melt Flow 21.3 g/10 min

@Load 2.16 kg,
Temperature 300 °C
21.3 g/10 min

@Load 4.76 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 19 g/10 min

@Load 2.16 kg,
Temperature 300 °C
19 g/10 min

@Load 4.76 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 148 MPa
21500 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.5 %
2.5 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 12.92 GPa
1874 ksi
5 mm/min; ASTM D638
Flexural Strength 231 MPa
33500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 11.7 GPa
1700 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.920 J/cm
1.72 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.01 J/cm
9.39 ft-lb/in
ASTM D4812