S&E Specialty Polymers TufTech™ SE11-031 PVC Compound
| Category | Polymer , Thermoplastic , Vinyl (PVC) |
| Manufacturer | S&E Specialty Polymers |
| Trade Name | TufTech™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | S&E Specialty Polymers TufTech™ SE11-031 PVC Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Application: Automotive - PVC, Integral Colored, Exterior Weatherable, Extrusion & Injection Molding CompoundInformation provided by S&E Specialty Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 - 1.37 g/cc | 1.31 - 1.37 g/cc | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 77.925 - 88.315 @Temperature 85.0 °C, Time 605000 sec |
77.925 - 88.315 @Temperature 185 °F, Time 168 hour |
Heat Aging; ISO 188, Method B |
| 75.0 - 85.0 @Time 15.0 sec |
75.0 - 85.0 @Time 0.00417 hour |
ISO 868 | |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | 500mm/min; ISO 527, 1A |
| 16.083 MPa @Temperature 85.0 °C, Time 605000 sec |
2332.6 psi @Temperature 185 °F, Time 168 hour |
Heat Aging; ISO 188, Method B | |
| Elongation at Break | 345 % | 345 % | 500mm/min; ISO 527, 1A |
| 370.875 % @Treatment Temp. 85.0 °C, Time 605000 sec |
370.875 % @Treatment Temp. 185 °F, Time 168 hour |
Heat Aging; ISO 188, Method B |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cold Flex | -34°C | SAE J323, Method A, No cracks, 12 mm mandrel |