SK Chemicals SKYTHANE® S185A Polyester Based Thermoplastic Polyurethane Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade
Manufacturer SK Chemicals
Trade Name SKYTHANE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SK Chemicals SKYTHANE® S185A Polyester Based Thermoplastic Polyurethane Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: SK Chemicals has supplied Thermoplastic Polyurethane Elastomer (TPU) under the name of SKYTHANE. Applications include:Keyboard CoversOutsoles of Soccer ShoesWire and CableAirbagsSheets and FilmHoses and TubingShoe ComponentsFire HosesInformation provided by SK Chemicals.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Shore A 87
87
ASTM D2240
Hardness, Shore D 36
36
ASTM D2240
Tensile Strength, Ultimate 39.2 MPa
5690 psi
ASTM D412
Elongation at Break 650 %
650 %
ASTM D412
100% Modulus 0.00689 GPa
1.00 ksi
ASTM D412
300% Modulus 0.0145 GPa
2.10 ksi
ASTM D412
Resilience 45
45
Vertical Rebound; ASTM D2632
Tear Strength 108 kN/m
616 pli
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 25
25
H18 wheel, 1000g load; ASTM D1044
Thermal Properties Metric English Comments
Vicat Softening Point 95.0 °C
203 °F
ASTM D1525
Processing Properties Metric English Comments
Processing Temperature 190 °C
374 °F
Transition Temperature
190 °C
374 °F
Metering Temperature
Middle Barrel Temperature 185 °C
365 °F
Nozzle Temperature 195 °C
383 °F
Zone 1 175 °C
347 °F
Zone 2 180 °C
356 °F
Zone 3 185 °C
365 °F
Zone 4 190 °C
374 °F
Adapter Temperature 190 °C
374 °F
Die Temperature 190 °C
374 °F
Tip
195 °C
383 °F
Body
Mold Temperature 20.0 - 40.0 °C
68.0 - 104 °F