Sharadaa Ceramics REFCAST LC90ABR Low Cement Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Sharadaa Ceramics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sharadaa Ceramics REFCAST LC90ABR Low Cement Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: We bring to our clients a range of Low Cement Castables, that are available in varied alumina content and service range. Designed for abrasion resistance application, these are widely used in furnaces such as ladle back up lining, sintering furnace roof and soaking pit covers.Information provided by Sharadaa Ceramics Pvt. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | >= 2.90 g/cc | >= 0.105 lb/in³ | Dried at 110°C |
| Grain Size | <= 10000 µm | <= 10000 µm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.0137 GPa @Temperature 110 °C |
1.99 ksi @Temperature 230 °F |
|
| 0.0177 GPa @Temperature 1100 °C |
2.57 ksi @Temperature 2010 °F |
||
| 0.0216 GPa @Temperature 1500 °C |
3.13 ksi @Temperature 2730 °F |
||
| Compressive Strength | 108 MPa @Temperature 110 °C |
15600 psi @Temperature 230 °F |
Cold Crushing |
| 127 MPa @Temperature 1100 °C |
18500 psi @Temperature 2010 °F |
Cold Crushing | |
| 147 MPa @Temperature 1500 °C |
21300 psi @Temperature 2730 °F |
Cold Crushing | |
| 29.4 MPa @Time 86400 sec |
4270 psi @Time 24.0 hour |
Cold Crushing |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.86 W/m-K @Temperature 800 °C, Time 10800 sec |
12.9 BTU-in/hr-ft²-°F @Temperature 1470 °F, Time 3.00 hour |
|
| 1.86 W/m-K @Temperature 400 °C, Time 10800 sec |
12.9 BTU-in/hr-ft²-°F @Temperature 752 °F, Time 3.00 hour |
||
| 1.98 W/m-K @Temperature 600 °C, Time 10800 sec |
13.7 BTU-in/hr-ft²-°F @Temperature 1110 °F, Time 3.00 hour |
||
| Maximum Service Temperature, Air | 1750 °C | 3180 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | >= 90 % | >= 90 % | |
| Fe2O3 | <= 0.60 % | <= 0.60 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Permanent Linear Change | -0.2 - 0.2% | 800°C |
| -0.3 - 0.3% | 1100°C | |
| -0.9 - 0.9% | 1500°C | |
| Refractoriness | >1820°C | |
| Thermal Expansion | 0.9 | 1000°C, Reversible |
| Water Required to Mix | 4 - 4.5% |
Users viewing this material also viewed the following:
- MV Labs PB700 Pb(NO3)2 Lead(II) nitrate
- NIZHNEKAMSKNEFTEKHIM PE 5118N (18601) Linear Low Density Polyethylene
- Huntsman DT 125-1 Matting Agent
- Samsung Cheil Industries Infino® HP-0500 ABS, Unreinforced Heat Resistant
- SABIC Innovative Plastics NORYL EXT115 PPE+PS (Asia Pacific)
- Zircar Zirconia YK-15 Yttria Knit Textile Insulation
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 6 PHR Varox DBPH-50
- Diamond Polymers ASA/PC 7030
- California Fine Wire Alloy 20-245 Precious Metal Alloy
- 3M Scotchcal™ ElectroCut™ 7725-263 Graphic Film
Copyright © lookpolymers.com All Rights Reserved