TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, No Plasticizer

Category Polymer , Thermoset , Polyester, TS , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Unreinforced , Rubber or Thermoset Elastomer (TSE)
Manufacturer TSE Industries, Inc
Trade Name Millathane®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, No Plasticizer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and many other high performance polyurethane applications. Millathane 76 can be vulcanized by sulfur or peroxide cured systems.Plasticizers should be used in all Millathane®76 compounds to better incorporate fillers and improve processing. Some plasticizers are not compatible with Millathane76, e.g. naphthenic and all paraffinic oils, however, a number of ester plasticizers perform very well.FormulationMillathane 76 100.0Zinc Stearate0.5N-550 Black40.0MBTS4.0MBT2.0Thanecure® ZM1.0Sulfur1.5All information provided by TSE Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 75
75
82
82
heat aged 70 hours @ 100ºC
Tensile Strength, Yield 25.19 MPa
3653 psi
Elongation at Yield 490 %
490 %
100% Modulus 0.00552 GPa
0.801 ksi
200% Modulus 0.01275 GPa
1.849 ksi
300% Modulus 0.01904 GPa
2.761 ksi
Tear Strength 63.0 kN/m
359 pli
Die C
Compression Set 32.3 %

@Temperature 70.0 °C,
Time 79200 sec
32.3 %

@Temperature 158 °F,
Time 22.0 hour
Thermal Properties Metric English Comments
Brittleness Temperature -35.0 °C
-31.0 °F
Processing Properties Metric English Comments
Cure Time 8.00 min

@Temperature 155 °C
0.133 hour

@Temperature 311 °F
Descriptive Properties Value Comments
Weight Loss (%) 1.5
heat aged 70 hours @ 100ºC