Washington Penn Homopolymer Polypropylene 20% Glass Reinforced

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler
Manufacturer Washington Penn
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Washington Penn Homopolymer Polypropylene 20% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Fiberglass & mineral-reinforced polypropylene compounds provide excellent tensile and impact properties. Mold shrinkage is similar to ABS and polystyrene. Compounds also have dimensional stability. The glass-reinforcement provides a better strength and modulus than any of the particulate mineral fillers.Information provided by Washington Penn Plastic Co.
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
ASTM D792
Filler Content 20 %
20 %
Melt Flow 11 g/10 min
11 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 66.2 MPa
9600 psi
ASTM D638
Elongation at Break 6.9 %
6.9 %
ASTM D638
Elongation at Yield 6.9 %
6.9 %
ASTM D638
Flexural Modulus 3.45 GPa
500 ksi
1% Secant; ASTM D790
3.65 GPa
530 ksi
Tangent; ASTM D790
Izod Impact, Notched 0.641 J/cm
1.20 ft-lb/in
ASTM D256
Gardner Impact 0.904 J

@Temperature 23.0 °C
0.667 ft-lb

@Temperature 73.4 °F
ASTM D5420
Impact 1.2
1.2
Dynatup Impact, in/in; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 157 °C
315 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 135 °C
275 °F
ASTM D648