Washington Penn Homopolymer Polypropylene 27% Glass Reinforced

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler
Manufacturer Washington Penn
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Washington Penn Homopolymer Polypropylene 27% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Fiberglass & mineral-reinforced polypropylene compounds provide excellent tensile and impact properties. Mold shrinkage is similar to ABS and polystyrene. Compounds also have dimensional stability. The glass-reinforcement provides a better strength and modulus than any of the particulate mineral fillers.Information provided by Washington Penn Plastic Co.
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
ASTM D792
Filler Content 27 %
27 %
Melt Flow 7.0 g/10 min
7.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 71.0 MPa
10300 psi
ASTM D638
Elongation at Break 7.2 %
7.2 %
ASTM D638
Elongation at Yield 7.2 %
7.2 %
ASTM D638
Flexural Modulus 4.31 GPa
625 ksi
1% Secant; ASTM D790
4.41 GPa
640 ksi
Tangent; ASTM D790
Izod Impact, Notched 0.694 J/cm
1.30 ft-lb/in
ASTM D256
Gardner Impact 0.904 J

@Temperature 23.0 °C
0.667 ft-lb

@Temperature 73.4 °F
ASTM D5420
Impact 3.2
3.2
Dynatup Impact, in/in; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 149 °C
300 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 141 °C
285 °F
ASTM D648