Zotefoams Plastazote® LD15 Low Density Polyethylene Foam

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Zotefoams
Trade Name	Plastazote®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zotefoams Plastazote® LD15 Low Density Polyethylene Foam.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Compliant with EC food contact and US FDA regulations.Information provided by Zotefoams

Physical Properties	Metric	English	Comments
Density	0.0150 g/cc	0.000542 lb/in³	Nominal skin/skin; BS ISO 7214 1998
	0.0140 - 0.0180 g/cc	0.000506 - 0.000650 lb/in³	sheet density
Cell Length	0.380 mm	0.0150 in	Typical Diameter
	0.200 - 0.600 mm	0.00787 - 0.0236 in

Mechanical Properties	Metric	English	Comments
Hardness, Shore OO	43	43	10 mm cell/cell thickness; ISO 868 1985
Tensile Strength	0.245 MPa	35.5 psi	ISO 7214 1998
Elongation at Break	110 %	110 %
Compressive Yield Strength	0.0260 MPa @Strain 10.0 %	3.77 psi @Strain 10.0 %	BS ISO 7214 1998
	0.0450 MPa @Strain 25.0 %	6.53 psi @Strain 25.0 %	BS ISO 7214 1998
	0.0750 MPa @Strain 40.0 %	10.9 psi @Strain 40.0 %	BS ISO 7214 1998
	0.107 MPa @Strain 50.0 %	15.5 psi @Strain 50.0 %	BS ISO 7214 1998
Tear Strength	0.330 kN/m	1.88 pli	BS EN ISO 8067 1995
Compression Set	7.0 % @Time 79200 sec, Strain 25.0 %	7.0 % @Time 22.0 hour, Strain 25.0 %	24 hr recovery; BS ISO 7214 1998
	15 % @Time 79200 sec, Strain 25.0 %	15 % @Time 22.0 hour, Strain 25.0 %	0.5 hr recovery; BS ISO 7214 1998
	23 % @Time 79200 sec, Strain 50.0 %	23 % @Time 22.0 hour, Strain 50.0 %	24 hr recovery; BS ISO 7214 1998
	31 % @Time 79200 sec, Strain 50.0 %	31 % @Time 22.0 hour, Strain 50.0 %	0.5 hr recovery; BS ISO 7214 1998

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.0387 W/m-K	0.269 BTU-in/hr-ft²-°F	mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air	95.0 °C	203 °F
Minimum Service Temperature, Air	-70.0 °C	-94.0 °F
Flammability Test	2.8 @Thickness 13.0 mm	2.8 @Thickness 0.512 in	Horizontal Burn Rate, mm/sec; ISO 7214 1998
	3.6 @Thickness 5.00 mm	3.6 @Thickness 0.197 in	Horizontal Burn Rate, mm/sec; ISO 7214 1998