Polymer Property : Linear Mold Shrinkage = 0.0080 in/in Product List

Physical Properties

Tips: 30 items are displayed at most.
Physical Properties Metric English Comments
Linear Mold Shrinkage 0.0080 cm/cm
0.0080 in/in
STN 64 0808
Plastcom SLOVAMID 66 GF 15 Polyamide 66, 15% Glass Fiber
FeaturesChemically reinforced with 15% glass fiber, suitable for mouldings with high strength and toughness also at low temperatures. Used in the automotive, engineering and electrical industry. W..
Linear Mold Shrinkage 0.0080 - 0.011 cm/cm

@Thickness 3.17 mm
 0.0080 - 0.011 in/in

@Thickness 0.125 in
Ovation Polymers Opnyl OP66UT105 Nylon 66
Ultra Tough - High Impact, Excellent retention of mechanical properties, High service temperature. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All..
Linear Mold Shrinkage 0.0080 - 0.020 cm/cm
0.0080 - 0.020 in/in
FRISETTA Test Method
Nilit FRIANYL A63 W-GV10 Nylon 6.6 for injection molding, 10% glass fiber reinforced
Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Linear Mold Shrinkage 0.0080 cm/cm
0.0080 in/in
AMMS; ISO 2577
Solvay Engineered Polymers SEQUEL® 2325 Engineered Polyolefin  (discontinued **)
Description: SEQUEL® 2325 engineered polyolefin is designed for mold-in-color automotive interior applications. This material exhibits excellent low-gloss surface appearance and processability. Ap..
Linear Mold Shrinkage 0.0080 - 0.010 cm/cm
0.0080 - 0.010 in/in
Across Flow; ISO 2577
Polykemi AB POLYfill PP EIP12030RF Polypropylene/EPDM, Mineral Reinforced
Information provided by Polykemi AB
Linear Mold Shrinkage 0.0080 cm/cm
0.0080 in/in
ASTM D955
Covestro Bayblend® 2773 Polycarbonate + ABS Blend, Automotive  (discontinued **)
Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ..
Linear Mold Shrinkage 0.0080 - 0.014 cm/cm
0.0080 - 0.014 in/in
Lehmann & Voss LUVOCOM® 1-8491 Polyamide 66, with carbon fiber, heat stabilized
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.High dimensionally stab..
Linear Mold Shrinkage 0.0080 cm/cm
0.0080 in/in
ASTM D995
Huntsman IROGRAN® A 85 P 4394 TPU-Polyether
Introduction: IROGRAN A 85 P 4394 is a high performance polyether based thermoplastic polyurethane intended for extrusion and injection molding applications. IROGRAN A 85 P 4394 is part of the HUNTS..
Linear Mold Shrinkage 0.0080 - 0.010 cm/cm
0.0080 - 0.010 in/in
3.2 mm; ASTM D955
Lavergne VYPET VNT 1020 Polyester-PC Alloy
The Vypet 1020 Black is a medium viscosity Polyester and PC alloy, has an excellent balance of stiffness and impact resistance.Features: Excellent Processability; Good Impact Resistance; Good Chemic..
Linear Mold Shrinkage 0.0080 - 0.011 cm/cm
0.0080 - 0.011 in/in
ASTM D955
Star Plastics PC/PBT7820 Molding Grade PC/PBT
Information provided by Star Plastics, Inc.
Linear Mold Shrinkage 0.0080 cm/cm
0.0080 in/in
mold average
Borealis Daplen™ ED230HP Polypropylene TPO Compound
Daplen™ ED230HP is a 20% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties and gives a good surfac..
Linear Mold Shrinkage 0.0080 - 0.010 cm/cm
0.0080 - 0.010 in/in
as molded
A. Schulman POLYTROPE™ TPP 608 Olefinic Elastomer
DescriptionPolytrope TPP 608 is an olefinic elastomer exhibiting low thermal expansion, low heat sag and high DOI on painted parts. ApplicationTPP 608 is designed specifically for automotive fascia..
Linear Mold Shrinkage 0.0080 - 0.010 cm/cm
0.0080 - 0.010 in/in
Polyram RamLloy PVB101 ABS/NYLON alloy, Impact Modified
Impact modified ABS/NYLON alloy for injection molding applicationsInformation provided by Polyram Ram On Ind.
Linear Mold Shrinkage 0.0080 - 0.012 cm/cm

@Thickness 3.175 mm
 0.0080 - 0.012 in/in

@Thickness 0.1250 in
 ASTM D955
A. Schulman SCHULAMID® 6 NV12 Easy Flow Low Viscosity Nylon 6
Information provided by A. Schulman.
Linear Mold Shrinkage 0.0080 - 0.011 cm/cm
0.0080 - 0.011 in/in
ASTM D955
A. Schulman POLYFORT™ FPP 1602 Glass Reinforced, Chemically Coupled Homopolymer
DescriptionPolyfort® FPP 1602 is a 10% glass reinforced chemically coupled homopolymer.Information provided by A. Schulman.
Linear Mold Shrinkage 0.0080 cm/cm
0.0080 in/in
± 0.1 after 60 min. at 120°C
A. Schulman POLYTROPE™ TPP 615 Olefinic Elastomer
DescriptionPolytrope TPP 615 is an olefinic elastomer developed to exhibit very low thermal expansion, high DOI on painted parts with good low temperature impact properties. ApplicationTPP 615 is de..
Linear Mold Shrinkage 0.0080 - 0.015 cm/cm
0.0080 - 0.015 in/in
ASTM D955
Cheng Yu Plastic NGCV2 Flame Retardant Nylon 6, 20% Mineral Reinforced
Linear Mold Shrinkage 0.0080 - 0.020 cm/cm
0.0080 - 0.020 in/in
ELASTO UK Dryflex® 500750S SEBS Based Material, Unfilled Qualities, 75A Hardness, Translucent
The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha..
Linear Mold Shrinkage 0.0080 - 0.020 cm/cm
0.0080 - 0.020 in/in
ELASTO UK Dryflex® 502900S SEBS Based Material, Unfilled Qualities, 90A Hardness, Black
The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha..
Linear Mold Shrinkage 0.0080 - 0.012 cm/cm

@Thickness 4.00 mm
 0.0080 - 0.012 in/in

@Thickness 0.157 in
CP-Polymer-Technik Wellamid® 6000 HWCP Nylon 6, Heat Stabilized, Dry
Information provided by CP-Polymer-Technik GmbH & Co. KG
Linear Mold Shrinkage 0.0080 - 0.012 cm/cm

@Thickness 4.00 mm
 0.0080 - 0.012 in/in

@Thickness 0.157 in
CP-Polymer-Technik Wellamid® 6000 S Nylon 6, Finely Crystalline, Conditioned
Information provided by CP-Polymer-Technik GmbH & Co. KG
Linear Mold Shrinkage 0.0080 - 0.012 cm/cm

@Thickness 4.00 mm
 0.0080 - 0.012 in/in

@Thickness 0.157 in
CP-Polymer-Technik Wellamid® 6000 S Nylon 6, Finely Crystalline, Dry
Information provided by CP-Polymer-Technik GmbH & Co. KG
Linear Mold Shrinkage 0.0080 - 0.012 cm/cm

@Thickness 4.00 mm
 0.0080 - 0.012 in/in

@Thickness 0.157 in
CP-Polymer-Technik Wellamid® 6600/42 HWCP Nylon 66, Polymer Modified, Heat Stabilized, Conditioned
Information provided by CP-Polymer-Technik GmbH & Co. KG
Linear Mold Shrinkage 0.0080 cm/cm
0.0080 in/in
E-Polymers SEPAZ® N3040IR Nanoclay 4% Impact Modified Nano Composite Resin
Nanocomposite: SEPAZ Nano PA6 nanocomposites have been prepared successfully in commercial scale through 'in situ' polymerization or melt extrusion. The unique performance properties of nanocomposi..
Linear Mold Shrinkage 0.0080 cm/cm
0.0080 in/in
MD; ASTM D955
Aclo Accutech Polypropylene Homopolymer HP0334M30L Mica Reinforced
Linear Mold Shrinkage 0.0080 - 0.010 cm/cm

@Thickness 4.00 mm
 0.0080 - 0.010 in/in

@Thickness 0.157 in
CP-Polymer-Technik Wellamid® 6000 GS 30 HWCP 30% Glass Sphere Filled Nylon 6, Heat Stabilized, Conditioned
Information provided by CP-Polymer-Technik GmbH & Co. KG
Linear Mold Shrinkage 0.0080 - 0.010 cm/cm
0.0080 - 0.010 in/in
ISO 2577
Polyram RamLloy PVB702 Nylon/ABS Alloy, Impact Modified
Impact modified, UV stabilized Nylon/ABS alloy for injection molding applications.Information provided by Polyram.
Linear Mold Shrinkage 0.0080 - 0.010 cm/cm
0.0080 - 0.010 in/in
With Flow; ISO 2577
Polykemi AB POLYfill PPH T5040 FC VT Polypropylene Homopolymer, Mineral Reinforced
Information provided by Polykemi AB