Polymer Property : Linear Mold Shrinkage, Transverse = 0.010 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	ISO Data (Dry)
BASF Capron® GR630 HS 30% Glass-Filled Nylon 66 (Conditioned) (discontinued **) Capron GR630 HS is a heat stabilized, 30% glass fiber reinforced polyamide 6,6 injection molding compound offering excellent strength, stiffness, creep resistance and dimensional stability. This ba..
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	ASTM-D1204
Kinlead PL11 Lamination Grade BOPP Plain Film (thickness: 20 Âµm) PL11 is a general, lamination grade BOPP plain film. It is transparent and non heat sealable. It is excellent for extrusion lamination. One side has corona treatment. It is widely used in laminating..
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	ASTM-D1204
Kinlead PM11 Metalizing Grade BOPP Plain Film (thickness: 35 Âµm) PM11 is a general, metalizing grade BOPP plain film. It is transparent and non heat sealable. It has good heat resistance and tensile strength, and it has excellent metal adhesion. One side has coro..
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	ASTM-D1204
Kinlead PT11 Adhesive Tape Grade BOPP Plain Film (thickness: 20 Âµm) PT11 is a general, adhesive tape grade BOPP plain film. It is transparent and non heat sealable. It has excellent glue adhesion, good dimensional stability, and high tensile strength. One side has c..
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	ASTM-D1204
Kinlead PT12 Adhesive Tape Grade BOPP Plain Film (thickness: 25 Âµm) PT12 is a super clear, adhesive tape grade BOPP plain film. It is transparent and non heat sealable. It has excellent glue adhesion and high clarity. One side has corona treatment. It is widely used..
Linear Mold Shrinkage, Transverse	0.010 - 0.030 cm/cm @Time 86400 sec	0.010 - 0.030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP MX06404 PP LNP LUBRICOMP* MX06404 is a compound based on Polypropylene resin containing 20% Glass Fiber and 15% PTFE. Added features of this material include: Heat Stabilized, Low Extractable, Wear Resistant...
Linear Mold Shrinkage, Transverse	0.010 - 0.030 cm/cm @Time 86400 sec	0.010 - 0.030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RX05487 PA 66 LNP* LUBRICOMP* RX05487 is a compound based on Nylon 66 containing 10% Aramid Fiber, 10% Lubricant. Added features of this material are: Low Warpage, Wear Resistant.
Linear Mold Shrinkage, Transverse	0.010 - 0.017 cm/cm @Thickness 0.750 - 2.30 mm	0.010 - 0.017 in/in @Thickness 0.0295 - 0.0906 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 310SE0 PBT (Europe-Africa-Middle East) VALOX 310SE0 is an unreinforced, flame retardant PBT injection moulding resin. Applications: electrical industry, bobbins, keyboard, switches and switch components and appliance housings.
Linear Mold Shrinkage, Transverse	0.010 - 0.040 cm/cm @Time 86400 sec	0.010 - 0.040 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-KON MX01739C PP LNP* SAT-KON* MX01739C is a compound based on Polypropylene containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Clean Compounding System.
Linear Mold Shrinkage, Transverse	0.010 - 0.030 cm/cm @Time 86400 sec	0.010 - 0.030 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Stat-kon TD000 LNP* Stat-kon* TD000 is a compound based on Polyurethane resin. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Transverse	0.010 cm/cm @Time 86400 sec	0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP MF008S PP LNP THERMOCOMP* MF008S is a compound based on Polypropylene resin containing 30% Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized.
Linear Mold Shrinkage, Transverse	0.010 - 0.012 cm/cm @Time 86400 sec	0.010 - 0.012 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP Thermocomp RF0057E PA 66 (Europe-Africa-Middle East) LNP* Thermocomp* RF0057E is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Non-Brominated & Non-Chlorinated Flame Retardant.Thi..
Linear Mold Shrinkage, Transverse	0.010 - 0.030 cm/cm @Time 86400 sec	0.010 - 0.030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP WFB62 PBT LNP* THERMOCOMP* WFB62 is a compound based on PBT resin containing 10% Glass Fiber, 10% Glass Bead. Added feature of this grade is: Low Warpage.
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in
Toyobo Vylopet® EMC630 PET/PBT Blend Key Feature: Flame retardant V-0 UL 94 classApplications: general and high rigidity componentsPET/PBT blends suggested for glossy surfaces. General features of Vylopet® include heat resistance, go..
Linear Mold Shrinkage, Transverse	0.010 cm/cm @Thickness 4.00 mm	0.010 in/in @Thickness 0.157 in
CP-Polymer-Technik Wellamid® 6000 GV 10 HWCP 10% Glass Fiber Nylon 6, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	DAM; ISO 294-4 2577
DuPont Performance Polymers Zytel® HTN FR52G30NH BK337 Polyphthalamide (PPA) (Unverified Data**) 30% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide Zytel HTNFR52G30NH BK337 is a 30% glass reinforced flame retardant lubricated high performance polyamide resin. It..
Linear Mold Shrinkage, Transverse	0.010 - 0.015 cm/cm @Time 86400 sec	0.010 - 0.015 in/in @Time 24.0 hour	ISO 294
Eurostar Staramide R1000EI2 PA66, Impact Modified, Injection Molded Staramide R1000EI2 is an Impact Modified Polyamide 66 Injection Molding Resin (also known as R1000HI010)Information provided by Eurostar.
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in
Eurotec® Tecodur® PB70 GR30 NL CA 01 PBT/PET 30% glass fiber reinforced Excellent stiffness and hardnessGood mechanical strengthGood creep and fatigue behaviorVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance..
Linear Mold Shrinkage, Transverse	0.010 cm/cm @Thickness 2.00 mm	0.010 in/in @Thickness 0.0787 in	ISO 294-4
DuPont Performance Polymers Hytrel® G3548L TPC-ET (Unverified Data**) Hytrel® G3548L is a low modulus grade with nominal hardness of 35D. It contains non-discoloring stabilizer. It can be processed by many conventional thermoplastic processing techniques like injec..
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in
Eurotec® Tecomid® NA40 MR30 NL PA 6.6 30% mineral reinforced Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good..
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	Sheet
BASF Ultradur® S 4090 GM11 5/5% Glass/Mineral Filled PBT Description: Is a PBT + ASA, injection-molding grades reinforced with 5% glass fiber/mineral, for laminar parts with high demands on dimensional stability and low warpage, e.g. lids, ventilation gri..
Linear Mold Shrinkage, Transverse	0.010 cm/cm @Diameter 2.00 mm	0.010 in/in @Diameter 0.0787 in	ISO 294-4
Ascend Performance Materials Vydyne® R228 Nylon 66, 40% Mineral Reinforced, Conditioned Vydyne® R228 is a 40% mineral-reinforced PA66 resin formulated for improved impact strength. Available in black, it is an injection-molding grade formulated to retain the inherent processing advant..
Linear Mold Shrinkage, Transverse	0.010 cm/cm @Thickness 2.00 mm	0.010 in/in @Thickness 0.0787 in	ISO 294-4
Ascend Performance Materials Vydyne® R513H Nylon 66, 13% Glass Filled, Conditioned (2.5% Moisture) Vydyne® R513H is general-purpose, 13% glass-reinforced, heat stabilized PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for machine feed, flow, and mold ..
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	ISO 2577
BASF Ultramid® KR 4355 G5 25% Glass Filled PA6/6T (Conditioned) Description: 25% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r..
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	ISO 2577
BASF Ultramid® KR 4355 G5 BK 00564 25% Glass Filled PA6/6T (Dry) Description: 25% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r..
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in
E-Polymers SEPAZ® N3040HI Nanoclay 4% High Impact Nano Composite Resin Nanocomposite: SEPAZ Nano PA6 nanocomposites have been prepared successfully in commercial scale through 'in situ' polymerization or melt extrusion. The unique performance properties of nanocomposi..
Linear Mold Shrinkage, Transverse	0.010 - 0.0135 cm/cm	0.010 - 0.0135 in/in
LATI Latiohm 66-10 H2 CNT G/35 PA66, 35% Glass Fiber Reinforced, Heat Stabilized Semiconductive/dissipative product based on Polyamide 66 (PA66). Heat stabilized. Carbon nanotubes. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North Ameri..
Linear Mold Shrinkage, Transverse	0.010 - 0.012 cm/cm @Time 86400 sec	0.010 - 0.012 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP DL002P PC LNP LUBRICOMP* DL002P is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Exceptional Processing, Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.010 - 0.030 cm/cm @Time 86400 sec	0.010 - 0.030 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY Z20001 PPO LNP* Lubriloy* Z20001 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, Flame Retardant.