Polymer Property : Linear Mold Shrinkage = 0.0020 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage	0.0020 cm/cm @Thickness 6.35 mm	0.0020 in/in @Thickness 0.250 in	ASTM D955
FiberfilÂ® J-60/20/FR Polypropylene Homopolymer, 20% Glass Reinforced, Flame Retardant Information provided by FIBERFIL Engineered Plastics
Linear Mold Shrinkage	0.0020 cm/cm @Thickness 3.17 mm	0.0020 in/in @Thickness 0.125 in	ASTM D955
FiberfilÂ® J-60/40 Polypropylene Homopolymer, 40% Glass Reinforced Information provided by FIBERFIL Engineered Plastics
Linear Mold Shrinkage	0.0020 cm/cm @Thickness 3.17 mm	0.0020 in/in @Thickness 0.125 in	ASTM D955
FiberfilÂ® J-60/40/E Polypropylene Homopolymer, 40% Glass Reinforced, Chemically coupled Information provided by FIBERFIL Engineered Plastics
Linear Mold Shrinkage	0.0020 - 0.0040 cm/cm @Thickness 3.20 mm	0.0020 - 0.0040 in/in @Thickness 0.126 in	48 hr at 80°C; ASTM D955
A. Schulman POLYPUR™ FPU 1380 Thermoplastic Polyurethane Compound Information provided by A. Schulman.
Linear Mold Shrinkage	0.0020 - 0.0040 cm/cm @Thickness 1.00 mm	0.0020 - 0.0040 in/in @Thickness 0.0394 in	Absolute Drying
Toyobo GLAMIDE® TY-502NZ 6T-Nylon GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Linear Mold Shrinkage	0.0020 - 0.0050 cm/cm @Thickness 3.00 mm	0.0020 - 0.0050 in/in @Thickness 0.118 in	Absolute Drying
Toyobo GLAMIDE® TY-791HT 6T-Nylon GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Linear Mold Shrinkage	0.0020 cm/cm @Thickness 3.20 mm	0.0020 in/in @Thickness 0.126 in	ASTM D955
Eastman Eastar 5011 Copolyester Eastar Copolyester 5011 is a glycol modified polyethylene terephthalate(PET). The modification is made by adding a second glycol, cyclohexanedimethanol (CHDM) during the polymerization stages. The s..
Linear Mold Shrinkage	0.0020 - 0.0040 cm/cm @Thickness 3.20 mm	0.0020 - 0.0040 in/in @Thickness 0.126 in	48 hr at 80°C; ASTM D955
A. Schulman POLYPUR™ FPU 1380 Thermoplastic Polyurethane Compound Information provided by A. Schulman.
Linear Mold Shrinkage	0.0020 - 0.0050 cm/cm @Thickness 3.20 mm	0.0020 - 0.0050 in/in @Thickness 0.126 in	aged 48 hrs at 121°C; ISO 294
A. Schulman FORMION™ FI 388 Ionomer Information provided by A. Schulman.